Nanostructured superhydrophobic films synthesized by electrodeposition of fluorinated polyindoles

  1. ,
  2. and
Univ. Nice Sophia Antipolis, CNRS, LPMC, UMR 7336, 06100 Nice, France; Fax: (+33)492076156; Tel: (+33)492076159
  1. Corresponding author email
Guest Editor: M. Canepa
Beilstein J. Nanotechnol. 2015, 6, 2078–2087. https://doi.org/10.3762/bjnano.6.212
Received 01 Aug 2015, Accepted 08 Oct 2015, Published 28 Oct 2015
Full Research Paper
cc by logo
Album

Abstract

Materials with bioinspired superhydrophobic properties are highly desirable for many potential applications. Here, nine novel monomers derived from indole are synthesized to obtain these properties by electropolymerization. These monomers differ by the length (C4F9, C6F13 and C8F17) and the position (4-, 5- and 6-position of indole) of the perfluorinated substituent. Polymeric films were obtained with C4F9 and C6F13 chains and differences in the surface morphology depend especially on the substituent position. The polyindoles exhibited hydrophobic and superhydrophobic properties even with a very low roughness. The best results are obtained with PIndole-6-F6 for which superhydrophobic and highly oleophobic properties are obtained due to the presence of spherical nanoparticles and low surface energy compounds.

Introduction

The number of studies about materials with superhydrophobic properties, characterized by extremely high water contact angles (θw) and low water adhesion or hysteresis (also known as “Lotus effect”), grows exponentially because of the importance for both the scientific and industrial community [1-6]. Superhydrophobic properties are quite common in nature, in both animals and plants, and allow them surviving against predators or hostile environments such as extremely humid or dry regions, for example [7-12]. Bioinspiration has shown the importance of developing structured surfaces in the presence of low surface energy materials that allow one to obtain more easily superhydrophobic properties with higher robustness [13-15]. Controlling the surface energy and the roughness is hence fundamental to achieve the superhydrophobicity.

All kind of materials can be used to reach superhydrophobicity, but conducting polymers have many advantages such as an easiness to functionalize and opto-electronic properties [16] with the possibility to introduce various dopants (smart materials) [17,18]. Conducting polymers are also exceptional materials for the control of surface nanostructures and wettability. First of all, nanostructures of extremely various shapes can be produced in solution by self-assembly [19-21] or directly formed on substrates by different strategies such as preferential growth [22], grafting [23], vapor phase polymerization [24], plasma polymerization [25] and electropolymerization [26-30]. The last method allows for a very quick and easy deposition of conducting polymer films while the formation of surface structures can be controlled by electrochemical parameters [26] and the used monomer [27]. In order to control the formation of surface nanostructures, the core responsible for the polymerization (such as thiophene, pyrrole or 3,4-ethylenedioxythiophene) [27-30] is probably the most important parameter. Then, the polymer can also be controlled by introducing hydrophobic/hydrophilic substituents or dopant agents [17,18,27-30]. In most of the cases, fluorocarbon or hydrocarbon chains were used to reach superhydrophobic properties.

Here, we report for the first time the formation of superhydrophobic properties from indole derivatives. Nine novel indole monomers substituted by fluorocarbon chains of different length (C4F9, C6F13 and C8F17) and in different positions (4-, 5- and 6-position of indole) were synthesized and electropolymerized (Scheme 1). We report the influence of the fluorocarbon chain length and the substituent position on the surface morphology and hydrophobicity.

[2190-4286-6-212-i1]

Scheme 1: Original indole monomers synthesized and used in this manuscript.

Results and Discussion

Electrodeposition

In order to develop structured polymeric films, the monomers were electropolymerized. First of all, it was necessary to determine the oxidation potential (Eox) of all the monomers. These Eox were determined by cyclic voltammetry and were found to be in the range of 0.9–1.3 V vs SCE for the functionalized monomers, as shown in Table 1. A cyclic voltammogram for Indole-6-F6 is shown in Figure 1, where it is possible to see the maximum peak of oxidation of the monomer. Then, the polymerization was followed from −0.7 V to a potential slightly lower than Eox (working potential Ew) by the same electrochemical method. Examples of cyclic voltammograms for the polyindoles are presented in Figure 2.

Table 1: Oxidation potential (Eox) and working potential (Ew) for each monomer by electrochemical process. Electropolymerization in 0.1 M of acetonitrile/Bu4NClO4.

monomer oxidation potential Eox (V) working potential Ew (V)
Indole 1.64 1.56
Indole-4-F4 1.30 1.23
Indole-5-F4 1.31 1.26
Indole-6-F4 1.13 1.08
Indole-4-F6 1.19 1.13
Indole-5-F6 1.15 1.10
Indole-6-F6 1.07 1.03
Indole-4-F8 1.14 1.08
Indole-5-F8 1.06 1.01
Indole-6-F8 0.99 0.96
[2190-4286-6-212-1]

Figure 1: Cyclic voltammogram of the monomer Indole-6-F6 (1 scan at 20 mV·s−1). Electropolymerization in 0.1 M of acetonitrile/Bu4NClO4.

[2190-4286-6-212-2]

Figure 2: Cyclic voltammogram of polyindoles. (a) Indole-6-F8, (b) Indole-6-F6 and (c) Indole-6-F4 (5 scans at 20 mV·s−1). Electropolymerization in 0.1 M of acetonitrile/Bu4NClO4.

These cyclic voltammograms show only little variation in the polymer oxidation and reduction peaks due to the low conductivity of the polymers. Also, the short length of the new oligomers formed during the electropolymerization process increases their solubility resulting in polymeric films with a very low thickness. This may be explained by the reaction of amine groups of indole with the H+ ions released during the electropolymerization process. For these reasons, the deposition method has been changed and the depositions have been then performed at constant potential and using different normalized deposition charges, Qs, (from 0 to 100 mC·cm−2) in order to better control the amount of polymer electrodeposited. However, polymeric films were obtained with all the monomers except that with C8F17 chains because their large size induced very huge steric hindrances during the reaction and the polymerization is not favorable.

Surface structures and wettability

The surface structures were characterized by scanning electron microscopy (SEM) and surface roughness measurements. The SEM images for Qs = 100 mC·cm−2 are given in Figure 3 and Figure 4 and the surface roughness measurements can be found in Table 2. First of all, the surfaces are not very rough, however differences were observed especially with the substituent positions. Even if some craters are observed on PIndole-4-F6, the substitution in the 4-position gives the less structured surfaces. By contrast, nanofibers are observed with the substituents in the 5-position (PIndole-5-Fn) and spherical particles in the 6-position (PIndole-6-Fn). This confirms previous works in which authors showed that the polymerization is favorable in the indole positions 2, 3, 5 and 7 [31,32]. Indeed, if the polymerization of indole is more favorable in certain positions, the location of the substituent may influence the polymerization and the way in which the monomers are linked to one another forming different structures. This work is also in agreement with the literature where the authors showed that due to preferable polymerization positions on indole, fiber structures can be obtained by interfacial polymerization because the polymerization is directional, while spheres are obtained when the polymerization is equal in all directions [33]. In this case, the polymerization of the fluorinated indoles seems to be directional for PIndole-5-Fn and proceeds equally in all directions for PIndole-6-Fn. For PIndole-4-Fn, the polymerization should not be favorable to form any structure on the surface. Previous works showed that one of the main parameters governing the surface roughness is the solubility of the oligomers formed in the first instance [26,34]. Hence, higher roughness of PIndole-6-Fn can be explained by the formation of longer polymer chains. PIndole-5-F4 and PIndole-6-F4 also showed an increase in roughness for normalized charges of 50 and 100 mC·cm−2 without significant changes in the wettability comparing the others polyindoles. In contrast, PIndole-4-F6 showed the same tendency as the other polymers in terms of conserving the same wettability even if their roughness only exhibited a significant increase at a normalized charge of 100 mC·cm−2.

[2190-4286-6-212-3]

Figure 3: SEM images at two different magnifications (5000× and 25000×) of the polyindoles substituted with C6F13 chains in the different positions.

[2190-4286-6-212-4]

Figure 4: SEM images at two different magnifications (5000× and 25000×) of the polyindoles substituted with C4F9 chains in the different positions.

Table 2: Arithmetic roughness (Ra), quadratic roughness (Rq) and apparent contact angles (θ) for the four probe liquids (water, diiodomethane, sunflower oil and hexadecane) for the polymers as a function of the normalized deposition charge.

polymer normalized deposition charge (mC·cm−2) Ra (nm) Rq (nm) θwater θdiiodomethane θsunflower θhexadecane
PIndole 12.5 13.0 15.9 73.2 30.5 13.3 0
25 10.8 13.2 71.5 25.3 12.0 0
50 14.3 16.9 71.5 23.0 14.6 0
100 21.9 31.0 69.8 27.2 10.9 0
PIndole-4-F6 12.5 15.5 19.5 109.2 83.1 57.7 65.1
25 12.9 15.8 110.0 89.3 65.7 69.3
50 12.7 15.2 112.4 88.8 77.0 72.4
100 45.2 65.4 109.9 82.3 68.1 72.0
PIndole-5-F6 12.5 8.7 13.4 117.1 98.7 78.8 75.3
25 9.5 19.0 116.3 100.7 92.5 73.8
50 8.5 18.1 122.1 99.8 96.8 77.5
100 17.7 31.2 124.8 103.3 87.0 74.8
PIndole-6-F6 12.5 17.5 25.3 146.5 106.5 92.1 79.8
25 11.6 18.3 149.3 111.3 86.9 87.7
50 22.1 33.4 159.0 116.3 107.1 93.3
100 26.3 38.9 158.9 117.6 107.3 92.6
PIndole-4-F4 12.5 17.0 20.8 96.7 75.2 39.6 45.6
25 16.5 20.2 99.5 83.3 59.4 52.3
50 16.6 19.6 100.2 78.8 53.4 60.3
100 15.4 18.9 98.7 78.1 59.6 43.4
PIndole-5-F4 12.5 36.8 50.2 107.6 85.7 68.0 48.8
25 50.2 67.0 106.4 86.9 84.6 74.4
50 117.0 158.9 108.4 85.7 70.2 61.4
100 150.6 194.2 106.0 92.6 75.0 71.1
PIndole-6-F4 12.5 76.1 99.8 127.1 114.9 97.1 88.6
25 71.5 98.8 142.9 122.7 106.7 97.7
50 174.5 243.3 133.1 119.5 103.3 93.3
100 153.3 202.9 131.2 120.2 100.8 93.4

The wettability properties (Table 2) are in agreement with the SEM images. The polymers PIndole-4-Fn are just slightly hydrophobic confirming the low effect of the surface structures for these polymers, independent of the fluorinated chain size. The polymers PIndole-5-Fn are more hydrophobic with apparent water contact angles (θwater) of 124.8° for a normalized deposition charge of 100 mC·cm−2. Here, the contact angles are not very high because the nanofibers are horizontally aligned on the substrate. By contrast, the polymers PIndole-6-Fn display extremely high θwater and also superhydrophobic properties for PIndole-6-F6, even with a low roughness. The differences between the θwater for the C6F13-polyindoles can be seen in Figure 5. Indeed, not only θwater of 159.0° were measured on this polymer, but also highly oleophobic properties with θhexadecane = 93.3°. Moreover, the polymer presents extremely low hysteresis and sliding angles for normalized charges of 50 and 100 mC·cm−2, as shown in Table 3. For all polymers, the wettability changed with the position of the substituent on indole due to the differences in the structuration and with the increase of the length of the fluorinated chains. The different normalized charges did not result in large variations of wettability for any probe liquid, however, the highest normalized charge (100 mC·cm−2) presented the best results for wettability and roughness in almost all polyindoles.

[2190-4286-6-212-5]

Figure 5: Image of a water droplet deposited on PIndole-4-F6, PIndole-5-F6 and PIndole-4-F6; Qs = 100 mC·cm−2.

Table 3: Dynamic water contact angles (hysteresis H and sliding angle α) for PIndole-6-F6 as a function of the normalized deposition charge.

normalized deposition charge (mC·cm−2) H (°) α (°)
12.5 sticky behavior
25 sticky behavior
50 2.1 20.6
100 0.8 9.5

In order to explain the effects of the surface structures on the wetting properties, it is first necessary to prepare smooth substrates with each polymer and determine the contact angles (θY) for each probe liquid. These contact angles are dependent on the solid–vapor (γSV), solid–liquid (γSL) and liquid–vapor (γLV) surface tensions following the Young equation [35] (cos θY = (γSV − γSL)/γLV). The smooth substrates were obtained by reducing the normalized deposition charge (Qs) to 1 mC·cm−2 in order to cover all the substrate by a very thin polymer layer while avoiding the formation of surface structures. The roughness and the apparent contact angles of these smooth substrates are given in Table 4 confirming their ultra-low roughness and wettability. These results show that the polymers with C6F13 fluorinated chains are intrinsically hydrophobic (θYwater > 90°) while the polymers with C4F9 fluorinated chains as well as the polyindoles without fluorinated chain are slightly hydrophilic (θYwater < 90°). As expected the polymers with C6F13 fluorinated chains have also the highest oleophobicity even if the oil contact angles are relatively low.

Table 4: Arithmetic roughness (Ra), quadratic roughness (Rq) and apparent contact angles (θ) for the four probe liquids (water, diiodomethane, sunflower oil and hexadecane) for the “smooth” polymers.

polymer Ra (nm) Rq (nm) θYwater θYdiiodomethane θYsunflower θYhexadecane
PIndole 6.3 8.8 79.9 47.3 0 0
PIndole-4-F6 6.6 9.5 97.5 51.3 41.5 25.6
PIndole-4-F4 7.3 9.4 78.7 35.6 16.0 0
PIndole-5-F6 6.4 9.8 96.8 60.4 47.3 37.9
PIndole-5-F4 6.3 8.1 81.4 44.9 0 0
PIndole-6-F6 6.8 9.5 99.4 66.8 50.7 44.1
PIndole-6-F4 7.8 10.1 81.1 45.7 19.5 0

Indeed, two equations (the Wenzel and the Cassie–Baxter equation) [36,37] depending on θY are very often used to explain the effect of the surface roughness on the wetting properties. In the Wenzel equation [36] (cos θ = r·cos θY, where r is a roughness parameter), the surface roughness can increase θ, but only if θY > 90°. Hence, it is possible to have an extremely high θwater, but the contact angle hysteresis (H) is usually high because the surface roughness increases also the solid–liquid interface and thereby, increasing the adhesion between the water drop and the surface. Only the Cassie–Baxter equation [37] (cos θ = rf·f·cos θY + f − 1, where rf is the roughness ratio of the substrate wetted by the liquid, f the solid fraction and (1 − f) the air fraction) can predict the superhydrophobicity of PIndole-6-F6, for example. Here, the presence of a high amount of air between the droplet and the substrate can lead to extremely high θwater with a very low H. In the case of PIndole-6-F6, the presence of the spherical nanoparticles formed on the surface during the polymerization allows to trap a high amount of air leading to superhydrophobic properties. These nanoparticles also induce a high increase of the surface oleophobicity, for example an increase of θhexadecane of 49.2°, from 44.1° on the smooth surface to 99.3° on the structured surface.

Conclusion

Here we report for the first time the possibility to obtain hydrophobic and superhydrophobic polymeric films with a very low roughness by electropolymerization of fluorinated indoles differing by the length (C4F9, C6F13 and C8F17) and the position (4, 5 and 6-position on indole) of the perfluorinated substituent. Polymeric films were obtained for C4F9 and C6F13 showing several differences mainly with the substituent position, affecting the surface morphology and the wetting properties. The best results were obtained with PIndole-6-F6 for which a superhydrophobic state with a self-cleaning condition and highly oleophobic properties were reached due to the presence of spherical nanoparticles and the fluorinated compounds on the surface. This work opens new ways in the formation of superhydrophobic polyindoles films by electrodeposition for future applications.

Experimental

Monomer synthesis and characterization

4-(aminomethyl)indole, 5-(aminomethyl)indole and 6-(aminomethyl)indole were purchased from Sigma-Aldrich. The monomers were synthesized by amidification between the corresponding (aminomethyl)indole and fluorinated acid (Scheme 2). More precisely, 0.26 g (1.4 mmol, 1 equiv) of N-(3-dimethylaminopropyl)-N′-ethylcarbodiimide hydrochloride (EDC) and 0.17 g of 4-dimethylaminopyridine (DMAP) (1.4 mmol, 1 equiv) were added to 20 mL of dichloromethane containing 1 equiv of the corresponding fluorinated acid. After stirring for 30 min, 0.2 g (1.4 mmol, 1 equiv) of the corresponding (aminomethyl)indole was added. The solution was stirred at room temperature for 24 h. The crude product was purified by column chromatography (stationary phase: silica gel; eluent: chloroform/methanol 95:5).

[2190-4286-6-212-i2]

Scheme 2: Synthesis way to the indole derivatives.

N-((1H-Indol-4-yl)methyl)-4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,11-heptadecafluoroundecanamide (Indole-4-F8): Yield 15%; yellow solid; mp 163.2 °C; 1H NMR (200 MHz, CD3OD) δ 7.32 (d, J = 8.0 Hz, 1H), 7.24 (d, J = 3.2 Hz, 1H), 7.06 (m, 1H), 6.93 (d, J = 6.8 Hz, 1H), 6.51 (dd, J = 3.2, 0.9 Hz, 1H), 4.65 (s, 2H), 2.55 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.38 (m, 3F), −115.74 (m, 2F), −122.87 (m, 6F), −123.75 (m, 2F), −124.52 (m, 2F), −127.29 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.45, 137.84, 130.34, 128.04, 125.64, 122.22, 119.39, 111.83, 100.41, 42.98, 28.1 (t, J = 23.1 Hz), 27.62 (t, J = 6.2 Hz); MS (70 eV) m/z: M+ 620 (82), C9H9N2+• 145 (100), C9H8N+• 130 (92), C8H8N+ 118 (52).

N-((1H-Indol-4-yl)methyl)-4,4,5,5,6,6,7,7,8,8,9,9,9-tridecafluorononanamide (Indole-4-F6): Yield 25%; yellow solid; mp 150.2 °C; 1H NMR (200 MHz, CD3OD) δ 7.32 (d, J = 8.0 Hz, 1H), 7.24 (d, J = 3.2 Hz, 1H), 7.06 (m, 1H), 6.92 (d, J = 7.0 Hz, 1H), 6.50 (dd, J = 3.2, 0.9 Hz, 1H), 4.65 (s, 2H), 2.55 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.43 (m, 3F), −115.74 (m, 2F), −122.93 (m, 2F), −123.91 (m, 2F), −124.60 (m, 2F), −127.36 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.43, 137.81, 130.32, 128.04, 125.64, 122.22, 119.38, 111.82, 100.41, 42.98, 27.90 (t, J = 22.5 Hz), 27.47 (t, J = 2.8 Hz); MS (70 eV) m/z: M+ 520 (25), C9H9N2+• 145 (100), C9H8N+• 130 (87), C8H8N+ 118 (59).

N-((1H-Indol-4-yl)methyl)-4,4,5,5,6,6,7,7,8,8,8-undecafluorooctanamide (Indole-4-F4): Yield 21%; yellow solid; mp 139.8 °C; 1H NMR (200 MHz, CD3OD) δ 7.32 (d, J = 8.1 Hz, 1H), 7.24 (d, J = 3.2 Hz, 1H), 7.06 (m, 1H), 6.93 (d, J = 7.6 Hz, 1H), 6.50 (dd, J = 3.2, 0.9 Hz, 1H), 4.65 (s, 2H), 2.55 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.69 (m, 3F), −115.98 (m, 2F), −125.63 (m, 2F), −127.31 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.37, 137.75, 130.26, 127.98, 125.58, 122.16, 119.32, 111.76, 100.35, 42.91, 27.82 (t, J = 22.1 Hz), 27.50 (t, J = 4.0 Hz); MS (70 eV) m/z: M+ 420 (40), C9H9N2+• 145 (95), C9H8N+• 130 (100), C8H8N+ 118 (65).

N-((1H-Indol-5-yl)methyl)-4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,11-heptadecafluoroundecanamide (Indole-5-F8): Yield 28%; yellow solid; mp 135.9 °C; 1H NMR (200 MHz, CD3OD) δ 7.47 (s, 1H), 7.33 (d, J = 8.4 Hz, 1H), 7.21 (d, J = 3.1 Hz, 1H), 7.04 (dd, J = 8.4, 1.6 Hz, 1H), 6.40 (dd, J = 3.1, 0.8 Hz, 1H), 4.49 (s, 2H), 2.53 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.40 (m, 3F), −115.74 (m, 2F), −122.90 (m, 6F), −123.77 (m, 2F), −124.60 (m, 2F), −127.36 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.32, 137.03, 129.90, 129.53, 126.06, 122.45, 120.51, 112.24, 102.24, 45.09, 27.82 (t, J = 21.4 Hz), 27.53 (t, J = 4.1 Hz); MS (70 eV) m/z: M+ 620 (4), C9H9N2+• 145 (100), C9H8N+• 130 (92), C8H8N+ 118 (47).

N-((1H-Indol-5-yl)methyl)-4,4,5,5,6,6,7,7,8,8,9,9,9-tridecafluorononanamide (Indole-5-F6): Yield 51%; yellow solid; mp 85.5 °C; 1H NMR (200 MHz, CD3OD) δ 7.47 (s, 1H), 7.33 (d, J = 8.3 Hz, 1H), 7.21 (d, J = 3.1 Hz, 1H), 7.03 (dd, J = 8.3, 1.6 Hz, 1H), 6.40 (dd, J = 3.1 Hz, 0.8 Hz, 1H), 4.44 (s, 2H), 2.47 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.45 (m, 3F), −115.74 (m, 2F), −122.95 (m, 2F), −123.93 (m, 2F), −124.60 (m, 2F), −127.36 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.38, 137.10, 129.97, 129.61, 126.13, 122.52, 120.58, 112.31, 102.31, 45.16, 27.86 (t, J = 22.8 Hz), 27.60 (t, J = 3.0 Hz); MS (70 eV) m/z: M+ 520 (35), C9H9N2+• 145 (100), C9H8N+• 130 (90), C8H8N+ 118 (54).

N-((1H-Indol-5-yl)methyl)-4,4,5,5,6,6,7,7,8,8,8-undecafluorooctanamide (Indole-5-F4): Yield 61%; yellow solid; mp 47.7 °C; 1H NMR (200 MHz, CD3OD) δ 7.47 (s, 1H), 7.33 (d, J = 8.4 Hz, 1H), 7.21 (d, J = 3.1 Hz, 1H), 7.04 (dd, J = 8.4, 1.6 Hz, 1H), 6.40 (dd, J = 3.1, 0.8 Hz, 1H), 4.44 (s, 2H), 2.47 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.67 (m, 3F), −115.97 (m, 2F), −125.60 (m, 2F), −127.21 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.32, 137.03, 129.91, 129.54, 126.07, 122.45, 120.52, 112.24, 102.25, 45.09, 27.78 (t, J = 22.5 Hz), 27.64 (t, J = 3.9 Hz); MS (70 eV) m/z: M+ 420 (98), C9H9N2+• 145 (90), C9H8N+• 130 (100), C8H8N+ 118 (70).

N-((1H-Indol-6-yl)methyl)-4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,11-heptadecafluoroundecanamide (Indole-6-F8): Yield 30%; yellow solid; mp 121.0 °C; 1H NMR (200 MHz, CD3OD) δ 7.49 (d, J = 8.1 Hz, 1H), 7.32 (s, 1H), 7.20 (d, J = 3.1 Hz, 1H), 6.95 (dd, J = 8.1, 1.4 Hz, 1H), 6.40 (dd, J = 3.1, 0.8 Hz, 1H), 4.45 (s, 2H), 2.56 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.39 (m, 3F), −115.76 (m, 2F), −122.86 (m, 6F), −123.78 (m, 2F), −124.58 (m, 2F), −127.29 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.36, 137.73, 132.46, 128.79, 125.87, 121.30, 120.22, 111.47, 102.17, 45.10, 27.79 (t, J = 21.0 Hz), 27.43 (t, J = 5.0 Hz); MS (70 eV) m/z: M+ 620 (4), C9H9N2+• 145 (100), C9H8N+• 130 (97), C8H8N+ 118 (45).

N-((1H-Indol-6-yl)methyl)-4,4,5,5,6,6,7,7,8,8,9,9,9-tridecafluorononanamide (Indole-6-F6): Yield 19%; yellow solid; mp 120.7 °C; 1H NMR (200 MHz, CD3OD) δ 7.49 (d, J = 8.1 Hz, 1H), 7.31 (s, 1H), 7.20 (d, J = 3.1 Hz, 1H), 6.94 (dd, J = 8.1, 1.5 Hz, 1H), 6.40 (dd, J = 3.1, 0.8 Hz, 1H), 4.45 (s, 2H), 2.47 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.45 (m, 3F), −115.77 (m, 2F), −122.95 (m, 2F), −123.93 (m, 2F), −124.60 (m, 2F), −127.36 (m, 2F); 13C NMR (50 MHz, CD3OD) δ 172.43, 137.80, 132.52, 128.86, 125.93, 121.36, 120.28, 111.54, 102.23, 45.15, 27.88 (t, J = 21.0 Hz), 27.58 (t, J = 3.5 Hz); MS (70 eV) m/z: M+ 520 (40), C9H9N2+• 145 (100), C9H8N+• 130 (94), C8H8N+ 118 (53).

N-((1H-Indol-6-yl)methyl)-4,4,5,5,6,6,7,7,8,8,8-undecafluorooctanamide (Indole-6-F4): Yield 33%; yellow solid; mp 105.7 °C; 1H NMR (200 MHz, CD3OD) δ 7.50 (d, J = 8.1 Hz, 1H), 7.31 (s, 1H), 7.20 (d, J = 3.2 Hz, 1H), 6.95 (dd, J = 8.1, 1.5 Hz, 1H), 6.40 (dd, J = 3.1, 0.8 Hz, 1H), 4.45 (s, 2H), 2.58 (m, 4H); 19F NMR (188 MHz, CD3OD) δ −82.66 (m, 3F), −115.91 (m, 2F), −125.60 (m, 2H), −127.27 (m, 2H); 13C NMR (50 MHz, CD3OD) δ 172.43, 137.72, 132.45, 128.78, 125.87, 121.29, 120.21, 111.47, 102.21, 45.08, 27.72 (t, J = 21.0 Hz), 27.56 (t, J = 4.0 Hz); MS (70 eV) m/z: M+ 420 (85), C9H9N2+• 145 (85), C9H8N+• 130 (100), C8H8N+ 118 (70).

Electrodeposition parameters

The polyindole films were electrodeposited by using a potentiostat (Autolab). For this, 2 cm2 gold plates were chosen as working electrode, a carbon rod as counter-electrode while saturated calomel (SCE) was taken as reference electrode. The electrolyte used was a 0.1 mol solution of tetrabutylammonium perchlorate (Bu4NClO4) in anhydrous acetonitrile. Before the electrodeposition, the solution was degassed under argon and 0.01 mol of monomer was introduced. After the electrodeposition, the coated substrates were washed three times in acetonitrile and slowly dried.

Polymer and surface characterization

The surface roughness (arithmetic Ra and quadratic Rq) were determined by using a Wyko NT 1100 optical microscope of Bruker. The data were obtained using the High Mag Phase Shift Interference (PSI) working mode, the objective 50× and the field of view (FOV) 0.5×.

The scanning electron microscopy images were obtained by using a 6700F microscope of JEOL.

The contact angles were determined by using a DSA30 goniometer of Krüss. Liquids of different surface tension were chosen to characterize the surface hydrophobicity and oleophobicity: water (γLV = 72.8 mN·m−1), diiodomethane (γLV = 50.0 mN·m−1), sunflower oil (γLV ≈ 31 mN·m−1) and hexadecane (γLV = 27.6 mN·m−1). The apparent contact angles (θ) were obtained by taken the angle at the triple point of a liquid droplet put on the substrate. The contact angle hysteresis (H) and sliding angle (α) were determined with the tilted-drop method. Here, a 6 µL liquid droplet was put on the substrate and the substrate was inclined until the droplet moving. The maximum inclination angle is α. The advanced (θadv) and receding (θrec) contact angles and by deduction the hysteresis H = θadv – θrec were taken just before the moving of the droplet, the angle in the moving direction being θadv and that in the opposite direction θrec.

Acknowledgements

This work was supported by CNPq, Conselho Nacional de Desenvolvimento Científico e Tecnológico - Brazil (Process No. 202280/2014-4). We thank Jean-Pierre Laugier (CCMA, UNS) for the SEM images.

References

  1. Liu, M.; Zheng, Y.; Zhai, J.; Jiang, L. Acc. Chem. Res. 2010, 43, 368–377. doi:10.1021/ar900205g
    Return to citation in text: [1]
  2. Simpson, J. T.; Hunter, S. R.; Aytug, T. Rep. Prog. Phys. 2015, 78, 086501. doi:10.1088/0034-4885/78/8/086501
    Return to citation in text: [1]
  3. Si, Y.; Guo, Z. Nanoscale 2015, 7, 5922–5946. doi:10.1039/C4NR07554D
    Return to citation in text: [1]
  4. Nishimoto, S.; Bhushan, B. RSC Adv. 2013, 3, 671–690. doi:10.1039/c2ra21260a
    Return to citation in text: [1]
  5. Rahmawan, Y.; Xu, L.; Yang, S. J. Mater. Chem. A 2013, 1, 2955–2969. doi:10.1039/C2TA00288D
    Return to citation in text: [1]
  6. Wang, J.-N.; Zhang, Y.-L.; Liu, Y.; Zheng, W.; Lee, L. P.; Sun, H.-B. Nanoscale 2015, 7, 7101–7114. doi:10.1039/C5NR00719D
    Return to citation in text: [1]
  7. Darmanin, T.; Guittard, F. Mater. Today 2015, 18, 273–285. doi:10.1016/j.mattod.2015.01.001
    Return to citation in text: [1]
  8. Koch, K.; Bhushan, B.; Barthlott, W. Prog. Mater. Sci. 2009, 54, 137–178. doi:10.1016/j.pmatsci.2008.07.003
    Return to citation in text: [1]
  9. Sun, M.; Watson, G. S.; Zheng, Y.; Watson, J. A.; Liang, A. J. Exp. Biol. 2009, 212, 3148–3155. doi:10.1242/jeb.033373
    Return to citation in text: [1]
  10. Bush, J. W. M.; Hu, D. L.; Prakash, M. Adv. Insect Physiol. 2007, 34, 117–192. doi:10.1016/S0065-2806(07)34003-4
    Return to citation in text: [1]
  11. Ju, J.; Bai, H.; Zheng, Y.; Zhao, T.; Fang, R.; Jiang, L. Nat. Commun. 2012, 3, 1247. doi:10.1038/ncomms2253
    Return to citation in text: [1]
  12. Andrews, H. G.; Eccles, E. A.; Schofield, W. C. E.; Badyal, J. P. S. Langmuir 2011, 27, 3798–3802. doi:10.1021/la2000014
    Return to citation in text: [1]
  13. Sarkar, A.; Kietzig, A.-M. Soft Matter 2015, 11, 1998–2007. doi:10.1039/C4SM02787F
    Return to citation in text: [1]
  14. Cha, T.-G.; Yi, J. W.; Moon, M.-W.; Lee, K.-R.; Kim, H.-Y. Langmuir 2010, 26, 8319–8326. doi:10.1021/la9047402
    Return to citation in text: [1]
  15. Huovinen, E.; Takkunen, L.; Korpela, T.; Suvanto, M.; Pakkanen, T. T.; Pakkanen, T. A. Langmuir 2014, 30, 1435–1443. doi:10.1021/la404248d
    Return to citation in text: [1]
  16. Beaujuge, P. M.; Reynolds, J. R. Chem. Rev. 2010, 110, 268–320. doi:10.1021/cr900129a
    Return to citation in text: [1]
  17. Xu, L.; Chen, Z.; Chen, W.; Mulchandani, A.; Yan, Y. Macromol. Rapid Commun. 2008, 29, 832–838. doi:10.1002/marc.200700891
    Return to citation in text: [1] [2]
  18. Taleb, S.; Darmanin, T.; Guittard, F. ACS Appl. Mater. Interfaces 2014, 6, 7953–7960. doi:10.1021/am501279h
    Return to citation in text: [1] [2]
  19. Santos, J. L.; Li, Y.; Culver, H. R.; Yu, M. S.; Herrera-Alonso, M. Chem. Commun. 2014, 50, 15045–15048. doi:10.1039/C4CC06056C
    Return to citation in text: [1]
  20. Pringle, J. M.; Ngamna, O.; Chen, J.; Wallace, G. G.; Forsyth, M.; MacFarlane, D. R. Synth. Met. 2006, 156, 979–983. doi:10.1016/j.synthmet.2006.06.009
    Return to citation in text: [1]
  21. D’Arcy, J. M.; Tran, H. D.; Tung, V. C.; Tucker-Schwartz, A. K.; Wong, R. P.; Yang, Y.; Kaner, R. B. Proc. Natl. Acad. Sci. U. S. A. 2010, 107, 19673–19678. doi:10.1073/pnas.1008595107
    Return to citation in text: [1]
  22. Chiou, N.-R.; Lu, C.; Guan, J.; Lee, L. J.; Epstein, A. J. Nat. Nanotechnol. 2007, 2, 354–357. doi:10.1038/nnano.2007.147
    Return to citation in text: [1]
  23. Im, S. G.; Yoo, P. J.; Hammond, P. T.; Gleason, K. K. Adv. Mater. 2007, 19, 2863–2867. doi:10.1002/adma.200701170
    Return to citation in text: [1]
  24. Vucaj, N.; Quinn, M. D. J.; Baechler, C.; Notley, S. M.; Cottis, P.; Hojati-Talemi, P.; Fabretto, M. V.; Wallace, G. G.; Murphy, P. J.; Evans, D. R. Chem. Mater. 2014, 26, 4207–4213. doi:10.1021/cm5014653
    Return to citation in text: [1]
  25. Tarrade, J.; Darmanin, T.; Taffin de Givenchy, E.; Guittard, F.; Debarnot, D.; Poncin-Epaillard, F. Appl. Surf. Sci. 2014, 292, 782–789. doi:10.1016/j.apsusc.2013.12.051
    Return to citation in text: [1]
  26. Poverenov, E.; Li, M.; Bitler, A.; Bendikov, M. Chem. Mater. 2010, 22, 4019–4025. doi:10.1021/cm100561d
    Return to citation in text: [1] [2] [3]
  27. Darmanin, T.; Guittard, F. Adv. Mater. Interfaces 2015, 2, 1500081/1–1500081/7. doi:10.1002/admi.201500081
    Return to citation in text: [1] [2] [3] [4]
  28. Mortier, C.; Darmanin, T.; Guittard, F. Macromolecules 2015, 48, 5188–5195. doi:10.1021/acs.macromol.5b01054
    Return to citation in text: [1] [2] [3]
  29. Yan, H.; Kurogi, K.; Mayama, H.; Tsujii, K. Angew. Chem., Int. Ed. 2005, 44, 3453–3456. doi:10.1002/anie.200500266
    Return to citation in text: [1] [2] [3]
  30. Mortier, C.; Darmanin, T.; Guittard, F. Adv. Eng. Mater. 2014, 16, 1400–1405. doi:10.1002/adem.201400212
    Return to citation in text: [1] [2] [3]
  31. Singh, V.; Chauhan, D. S.; Pandey, P. C. A comparative study on electrochemical synthesis of carboxylic acid substituted indoles and their application in selective oxidation of dopamine.. IEEE Sensors 2009, Christchurch, New Zealand, Oct 25–28, 2009; pp 1140–1144. doi:10.1109/ICSENS.2009.5398578
    Return to citation in text: [1]
  32. Ma, X.; Zhou, W.; Mo, D.; Wang, Z.; Xu, J. Synth. Met. 2015, 203, 98–106. doi:10.1016/j.synthmet.2015.02.025
    Return to citation in text: [1]
  33. Yakhmi, J. V.; Saxena, V.; Aswal, D. K. Conducting Polymer Sensors, Actuators and Field-Effect Transistors. Functional Materials: Preparation, Processing and Applications; Elsevier, 2012; pp 61–110. doi:10.1016/B978-0-12-385142-0.00002-7
    Return to citation in text: [1]
  34. Mortier, C.; Darmanin, T.; Guittard, F. ChemPlusChem 2014, 79, 1434–1439. doi:10.1002/cplu.201402187
    Return to citation in text: [1]
  35. Young, T. Philos. Trans. R. Soc. London 1805, 95, 65–87. doi:10.1098/rstl.1805.0005
    Return to citation in text: [1]
  36. Wenzel, R. N. Ind. Eng. Chem. 1936, 28, 988–994. doi:10.1021/ie50320a024
    Return to citation in text: [1] [2]
  37. Cassie, A. B. D.; Baxter, S. Trans. Faraday Soc. 1944, 40, 546–551. doi:10.1039/tf9444000546
    Return to citation in text: [1] [2]
Other Beilstein-Institut Open Science Activities