Confirming exceptionally high level of publishing standards

 
 

Advances in the fabrication of graphene transistors on flexible substrates

Gabriele Fisichella1, Stella Lo Verso2, Silvestra Di Marco2, Vincenzo Vinciguerra2, Emanuela Schilirò1, Salvatore Di Franco1, Raffaella Lo Nigro1, Fabrizio Roccaforte1, Amaia Zurutuza3, Alba Centeno3, Sebastiano Ravesi2 and Filippo Giannazzo1
1CNR-IMM, VIII Strada 5, 95121 Catania, Italy
2STMicroelectronics, Stradale Primosole 50, 95121 Catania, Italy
3Graphenea, Tolosa Hiribidea 76, Donostia-San Sebastian, Spain
Email of corresponding author Corresponding author email     
This article is part of the Thematic Series "Self-assembly of nanostructures and nanomaterials II".
Guest Editor: I. Berbezier
Beilstein J. Nanotechnol. 2017, 8, 467–474.
doi:10.3762/bjnano.8.50
 
 
 
 

Abstract

Graphene is an ideal candidate for next generation applications as a transparent electrode for electronics on plastic due to its flexibility and the conservation of electrical properties upon deformation. More importantly, its field-effect tunable carrier density, high mobility and saturation velocity make it an appealing choice as a channel material for field-effect transistors (FETs) for several potential applications. As an example, properly designed and scaled graphene FETs (Gr-FETs) can be used for flexible high frequency (RF) electronics or for high sensitivity chemical sensors. Miniaturized and flexible Gr-FET sensors would be highly advantageous for current sensors technology for in vivo and in situ applications. In this paper, we report a wafer-scale processing strategy to fabricate arrays of back-gated Gr-FETs on poly(ethylene naphthalate) (PEN) substrates. These devices present a large-area graphene channel fully exposed to the external environment, in order to be suitable for sensing applications, and the channel conductivity is efficiently modulated by a buried gate contact under a thin Al2O3 insulating film. In order to be compatible with the use of the PEN substrate, optimized deposition conditions of the Al2O3 film by plasma-enhanced atomic layer deposition (PE-ALD) at a low temperature (100 °C) have been developed without any relevant degradation of the final dielectric performance.

Keywords: atomic layer deposition; chemical sensing; field effect transistor; flexible electronics; graphene

Top

Introduction

One of the new challenges in the field of electronics is represented by flexible devices. The evolution of the processing technologies for soft substrates and the discovery of new materials suitable for bending, stretching or conformably shaping [1], such as in the case of many 2D materials [2], paved the way to a huge number of stretchable, foldable or form factor reconfigurable demonstrators. Such devices can be considered for various applications, from consumer devices [3] to biomedical in vivo applications [4,5]. Among all the two-dimensional materials, graphene is one of the most appealing to be used as a flexible, conductive membrane, given its Young’s modulus on the order of TPa and large spring constant (1–5 N/m) [6]. Besides its high charge mobility of up to thousands of cm2·V−1·s−1, even at room temperature for both electron and holes, graphene is characterized by exhibiting only a small variation in electrical performance under mechanical deformation [7,8]. These are essential characteristics for stable and reliable operation.

Thanks to these properties, graphene can be considered for high frequency FETs both on conventional substrates [9] and on flexible platforms [10]. In particular, remarkable cut-off frequency values (≈25 GHz) and robust performance under repeated bending (down to 0.7 mm bending radius) have been reported in graphene FETs (Gr-FETs) even with gradually scaled (≈0.5 µm) channel lengths fabricated on a flexible polyimide substrate and adopting a back-gate configuration and Al2O3 as a gate dielectric.

In addition, due to the low density of states (DOS) around the Dirac point, the carrier density of graphene is very sensitive to the adsorption of charged/polar species at or near its surface – a peculiarity particularly suitable for chemical/biological sensing. As an example, gas sensors with single molecule sensitivity have been initially demonstrated using high quality, exfoliated graphene from graphite [11]. Considering the scalable graphene production methods, epitaxial graphene grown on silicon carbide has also been demonstrated as an excellent material for sensing [12]. However, for many applications, flexible and disposable sensors are needed. For these applications graphene has to be easily transferred to the target substrate. In this sense, the use of graphene grown by chemical vapor deposition (CVD) on various metals (Ni [7], Cu [13]) and using various precursors [14] represents the most suitable choice.

Among the various device architectures, Gr-FET-based sensors can represent a great combination between a chemical-to-electrical signal converter and an electrical signal amplifier [15]. In particular, the first characteristic can be achieved by using a properly extended channel area able to effectively interact with the chemical target, while the second one can be obtained by maximizing the gate capacitance. For this last reason, from a purely research perspective, the best device configuration is the ion sensing FET (IS-FET) [16] constituted of a graphene channel covered by the target solution and a macroscopic reference electrode immersed in the solution itself as the gate contact. Beside the fabrication simplicity, this configuration exploits electric double layer capacitance at the gate/solution interface and at the channel/solution interface, which can reach tens of µF/cm2 (depending on the ions concentration). However, for real applications, especially for a potential totally flexible device, there is a need of a reference electrode that is an external, rigid and macroscopic element, which represents a relevant drawback. The solid IS-FET [17] (where a local back-gate buried under a solid dielectric film replaces the reference electrode) represents a valid alternative for real applications. In this case the thickness and the dielectric constant of the insulating film have crucial importance in order to maintain a reasonably high gate capacitance of the final device. In particular, considering high κ-dielectrics such as HfO2 or Al2O3 with film thickness in the order of 10 nm, the gate capacitance can reach hundreds or even thousands of nF/cm2, which is still reasonably high for sensing applications. It is clear that the high quality and the scaled thickness of the dielectric film fabricated below the temperature limit of the plastic support is the key point for the final devices performance.

A low temperature (100 °C) deposition process to obtain a high quality dielectric film is essential in order to be compatible with common plastic substrates, such as poly(ethylene terephthalate) (PET) or poly(ethylene naphthalate) (PEN), which is also the case of our study.

Atomic layer deposition (ALD) represents an optimal method to fabricate a good quality Al2O3 dielectric film with a tight control on the deposited thickness and a high level of conformal coverage. While the thickness control allows easy fabrication of a tens of nanometer thick dielectric film (resulting in a beneficially high dielectric capacitance), the conformal coverage is essential to contain the potential local degradation of the dielectric performance. Otherwise, this degradation can take over due to the device topography and the high starting roughness of the plastic substrate.

ALD is essentially a low temperature process. It is possible to obtain a high quality Al2O3 film by depositing using a plasma-enhanced ALD process and exploiting trimethylaluminium (TMA) as the metalorganic chemical precursor and O2 as the co-reagent at an optimal growth temperature of 250 °C. Nevertheless, such a temperature is still high in combination with a plastic substrate such as PEN, for which the glass transition temperature is ≈155 °C. Using ALD it is possible to grow at lower temperatures as reported in the case of plastic coating and gas diffusion barrier fabrication [18]. However, with reducing the temperature, the deposition conditions must be optimized in order to ensure the expected layer-by-layer ALD mechanism of the insulating film, instead of a massive CVD growth mechanism, which in turn can result in a degradation of the overall structural and electrical quality of the insulator. This aspect is particularly relevant for the fabrication of a FET where the properties of the gate dielectric (e.g., permittivity, leakage current, critical breakdown field) are crucial for the device operation.

Top

Results and Discussion

Low temperature gate dielectric

In our experiments we developed a 100 °C PE-ALD process using a PE ALD LL reactor by SENTECH Instruments GmbH, starting with trimethylaluminium (TMA) as a metal-organic chemical precursor and O2 as the oxygen source for the Al2O3 synthesis. In particular, we explored the resulting properties obtained by modifying the deposition cycle and enlarging the purging periods between the precursor exposure in order to prevent the precursor mixing and a consequent CVD growth mechanism.

The developed low temperature (LT) and prolonged cycle process was analyzed on a silicon (100) reference wafer and compared to a standard temperature (ST) PE-ALD growth process. The morphology collected by tapping mode atomic force microscopy (tAFM) for the LT growth (Figure 1a left) is comparable to the morphology obtained by the ST growth (Figure 1a right). The dielectric thickness and the consequent growth per cycle was determined by spectroscopic ellipsometry measurements performed on an array of several positions on a wafer scale. A thickness of 28.9 ± 0.5 nm after 250 ALD cycles (0.12 nm/cycle growth rate) was revealed by the ST process, whereas after the same number of cycles, the LT process revealed a thickness of 40.9 ± 0.5 nm (0.16 nm/cycle growth rate).

[2190-4286-8-50-1]
Figure 1: a) Comparison between tapping mode atomic force microscopy (tAFM) morphologies of low temperature (left) and standard temperature (right) dielectric materials deposited on a Si wafer; b) AFM local step height of the lift-off patterned low temperature dielectric; c) comparison between tAFM morphologies of low temperature (left) and standard temperature (right) dielectric material deposited on an Al coated Si wafer; and d) current density leakage through low temperature and standard temperature dielectric materials.

The LT process thickness was also confirmed (43 ± 1 nm) by the local step height measure reported in Figure 1b for a patterned Al2O3. The dielectric patterning was obtained by depositing the oxide on a silicon wafer masked by a negative profile resist and then removing the resist by an ultrasonic hot chemical bath. This approach, namely the lift-off method, allows a structured layer to be defined without direct chemical/physical etching of the patterned layer. This completely avoids incomplete or over etching, resulting in a step profile which corresponds to the patterned layer thickness. It should be noted that this method is allowed only for the LT process if a standard resist for lift-off process is considered [19]. The 250 °C used in the ST process would totally degrade the resist.

Both LT and ST processes were repeated on an aluminum-coated silicon wafer, where a number of cycles was needed to produce a ≈30 nm dielectric thickness. The Al-coated Si wafer was prepared by depositing a 200 nm thick Al film by RF reactive sputtering with a surface roughness (measured by AFM, image not reported) of about 4.3 nm. The RMS roughness values obtained for both the LT Al2O3 (Figure 1c, left) and the ST Al2O3 (Figure 1c, right) were 4.20 nm and 4.49 nm, respectively, that is, very similar to the starting Al surface roughness.

The Al/Al2O3 stack was exploited for a mercury probe measurement of the dielectric capacitance. In particular, a metal–insulator–metal capacitor (MIM) is defined by the Al/Al2O3 stack from one side and from the reversibly contacted mercury probe on the other side. A wafer-scale matrix of sampled positions were collected on both the ST and the LT dielectric layers. Dielectric constants of 7.94 ± 0.05 and 7.91 ± 0.05 where extracted for ST and LT dielectrics, respectively, confirming a similar dielectric quality of the two films and an extremely good homogeneity of the result on the wafer scale (standard deviation below 1%). As reported in Figure 1d the leakage current through the dielectric was also extracted. In both cases, a negligible current on the order of hundreds of nA/cm2 (see Table 1) was collected for electric fields up to 6 MV/cm, which is a reasonable operating range. It is possible to conclude that the LT film obtained by a proper modification of the deposition parameters reveals a dielectric quality close to that obtained by a ST film and is good enough to be exploited as a dielectric material for FETs on plastic.

Table 1: Comparison between the low temperature and standard temperature process properties extracted during the material characterization on the standard Si substrates.
 Low temperature (100 °C)Standard temperature (250 °C)
Growth per Cycle:  
* Ellipsometry0.16 nm/cycle0.12 nm/cycle
* Local step height0.168 nm/cycle
Relative permittivity7.917.95
Leakage (6 MV/cm)6.6 × 10−7 A/cm21.1 × 10−7 A/cm2
Roughness (RMS):  
* On Si wafer0.297 nm0.443 nm
* On sputtered Al4.20 nm4.49 nm

Fabrication and electrical characterization of Gr-FETs on flexible substrates

We fabricated several arrays of independently back-gated Gr-FETs by adopting a specifically optimized process flow. In particular, we considered large area devices with channel widths and lengths on the order of ≈100 µm, suitable for solution sensing applications. This channel size poses a challenge considering that the larger the channel dimension, the higher the effect can be on the device performance due to the material defects (e.g., graphene cracks and grain boundaries, surface asperities, dielectric inhomogeneity).

We started with a thermally flattened PEN Teonex film purchased from Dupont Teiji Films. PEN is an analogous material to poly(ethylene terephthalate) (PET), with superior physical and thermal stability (up to 155 °C), which are advantageous properties for flexible technology.

The polymer film was reversibly bonded on a Si wafer by mechanical lamination, adopting a double face thermal release tape (Nitto Denko, 150 °C thermal release) and shaped by cutting along the wafer edges. This is essential for proper manageability of the substrate during fabrication and testing.

The polymer film, as reported in Figure 2a, was morphologically characterized by tAFM and a starting RMS of ≈7 nm was found. It is worth noting that even if this is a reasonable roughness for a plastic substrate, it is 1–2 orders of magnitude higher than the RMS values of traditional rigid substrates for electronics, such as silicon dioxide on Si.

[2190-4286-8-50-2]
Figure 2: a) Tapping mode atomic force microscopy (tAFM) morphology of the PEN surface and b) a schematic representation of the PEN starting substrate. c) tAFM morphology of the PEN-coated surface by a 100 nm protective Al2O3 layer and d) a schematic representation of the Al2O3 barrier/PEN substrate.

The polymer film surface was coated by a 100 nm protective Al2O3 layer, deposited by DC-pulsed RF reactive sputter, assisted by a cooling system able to maintain the sample below 100 °C. This is a relevant precaution in order to prevent polymer degradation which may occur due to the processing, in particular, where a plasma is involved. The tAFM morphology reported in Figure 2c shows an essentially unchanged morphology of the substrate surface after the protective coating deposition. This is an important indication of the absence of polymer degradation during the integration of the protective barrier. Figure 2d reports the schematic representation of the PEN substrate after the Al2O3 barrier integration.

200 nm thick aluminum back gate pads have been fabricated by metal sputtering, considering the same metal deposition process previously exploited on Si during the dielectric layer testing, and patterning by a lift-off approach. The metal morphology is reported in Figure 3a, revealing an RMS of ≈9.8 nm, consistent with the roughness of the underlying substrate. Figure 3b reports the schematic illustration of the patterned Al pads on the plastic substrate.

[2190-4286-8-50-3]
Figure 3: a) Tapping mode atomic force microscopy (tAFM) morphology and b) schematic illustration of the aluminum back-gate pad. c) tAFM morphology and d) related schematic illustration of the Al2O3 deposited by the low temperature ALD process.

A ≈30 nm thick Al2O3 dielectric film was deposited by the previously analyzed LT ALD process. The surface tAFM morphology reported in Figure 3c shows a roughness of ≈7.6 nm, slightly lower than the underlying Al gate contact. The absence of substrate morphological degradation demonstrates that the previously discussed LT process is completely compatible with the final plastic substrate.

Graphene transistor channels were fabricated starting from a single layer graphene film grown by CVD on large area copper foils (provided by Graphenea). The graphene membrane was transferred to a large area (100 mm diameter) of the target substrate by a PMMA-assisted wet transfer procedure and patterned by soft O2 plasma etching.

Figure 4a shows the tAFM morphology of graphene. The typical, wrinkled morphology of CVD-synthesized graphene [13] is less evident on PEN substrates compared with smoother substrates. However, it is still possible to identify wrinkles, as indicated by the dashed green circle in Figure 4a. A schematic illustration of the graphene channel fabricated over the FET gate contact is reported in Figure 4b.

[2190-4286-8-50-4]
Figure 4: a) Tapping mode atomic force microscopy (tAFM) morphology and b) schematic illustration of the graphene channel. c) Optical microscopy and d) schematic illustration of the final back-gated device with the detail of the involved series resistance contributions from source to drain.

After patterning the graphene channel, the source and drain contacts were fabricated by lift-off of a 30/120 nm thick Ni/Au double layer, which partially overlaps the edges of the graphene channel. A complete Gr-FET device is shown in the optical microscopy image in Figure 4c and schematically illustrated in Figure 4d. Furthermore, the resistance contributions which determine the total electrical resistance, RTOT, between source and drain contacts are also illustrated in Figure 4d. Here, the gate-bias-dependent graphene channel resistance, Rch(Vg), the source and drain contact resistance, Rc, and the access resistance, Racc, associated with the ungated graphene access regions between the channel and the source and drain contacts (Lacc = 20 µm length per access region) are shown.

The total resistance resulting from the series combination of these contributions can be expressed as:

[2190-4286-8-50-i1](1)

The capacitance of the Al2O3 dielectric deposited by ALD on the flexible substrate was characterized by metal–insulator–metal (MIM) test devices properly manufactured together with the Gr-FETs, into the same wafer. The resulting gate capacitance per unit area is Cg = 2.05 × 10−7 F/cm2. The Al2O3 film thickness of 29.9 nm is known from the growth rate previously determined on the reference substrate. The resulting dielectric constant is 6.9, which is reasonably high considering the low temperature (100 °C) adopted for the dielectric growth and the high roughness of the substrate. As a way of comparison with silicon dioxide, the resulting equivalent oxide thickness (EOT) is 16.8 nm.

Several arrays of independently biased back-gated Gr-FETs with different channel geometries were fabricated on the wafer scale using the above described process flow. The electrical characterization of more than 50 devices revealed a significant number of early failures. The origin of these failures is out of the scope of this paper and will be the subject of further investigations. Interestingly, working devices showed quite reproducible electrical characteristics.

Figure 5a reports the output characteristics (drain current vs drain bias, Id vs Vd) at incremental values of the back gate bias (Vg from 0 to 11 V) for a representative Gr-FET device with channel width W = 100 µm, channel length L = 190 µm (area = W × L = 19 × 103 µm2) and an access region length Lacc = 20 µm, defined as the distance between source (drain) and the channel region. All the output characteristics exhibit a linear (ohmic) behavior, with a gradually decreasing slope (i.e., an increasing channel resistance) in the considered gate bias range.

[2190-4286-8-50-5]
Figure 5: a) IdVd characteristics at different back gate bias values and b) IdVg transfer characteristic for a representative Gr-FET with channel width W = 100 μm, channel length L = 190 μm and access regions length Lacc = 20 μm. In the insert of b) the leakage current (Ig vs Vg) collected simultaneously to the transfer characteristic measurement is shown.

Figure 5b shows a representative transfer characteristic of the Gr-FET, i.e., Id vs Vg for a fixed drain bias (Vd = 0.1 V). It shows the typical ambipolar behavior for a graphene channel with a current minimum at the neutrality (or Dirac) point (VNP) at 9.0 V. The neutrality point is significantly shifted at high positive bias with respect to the expected ideal value calculated considering the difference between Al and neutral graphene workfunctions (VNP,id = WAlWGr ≈ 4.1 − 4.5 = −0.4 eV). This positive shift is a clear indication of graphene p-type doping, as estimated by p = Cg(VNPVNP,id)/q ≈ 1.2 × 1013 cm−2 [20], where q is the electron charge. This doping can be ascribed to the effect of the chemical (PMMA) residues which normally persist after the graphene transfer. It is worth noting that due to the constrains imposed by the use of a PEN substrate, it is not possible to perform thermal annealing processes (in vacuum or Ar/H2 ambient at temperatures from 300 to 400 °C) or stronger chemical treatments typically used to remove polymeric residues after graphene transfer on standard substrates. Furthermore, a certain doping can be attributed to the electrostatic effect of fixed or trapped charges in the gate oxide when deposited at low temperature.

The insert of Figure 5b shows the leakage current through the gate dielectric (Ig vs Vg) collected simultaneously to the transfer characteristic measurement, showing only a negligible current flow (less than nA) in the whole back gate bias range. The transfer conductance gm of the Gr-FET reported in Figure 6 was obtained considering the Id vs Vg characteristic by the formula:

[2190-4286-8-50-i2](2)

From the peak transfer conductance, we calculated the hole and electron field effect mobility, µh = 476 cm2·V−1·s−1 and µe = 204 cm2·V−1·s−1 using the formula:

[2190-4286-8-50-i3](3)
[2190-4286-8-50-6]
Figure 6: Transfer conductance, gm, of the Gr-FET, calculated from the Id vs Vg transfer characteristic.

These field effect mobility values are reasonably high, considering the channel area (about 104 µm2), the high roughness due to the plastic substrate and the unintentional doping of graphene. In particular, it is expected that the polycrystalline nature of CVD graphene has a direct effect on the current transport in a large area channel. In addition to these natural defects originating from CVD growth, the graphene membrane is subjected to significant strain if transferred to a rough surface while a certain amount of mechanical defects, such as cracks or folding is expected by the transfer procedure itself, especially onto a structured surface. Besides these macroscopic defects, nanoscale scattering mechanisms [21], such as charged impurities scattering and resonant scattering by defects/polymer contaminations, is expected to play a key role in reducing graphene mobility. Finally, it should also be noted that this is a calculation of the extrinsic field effect mobility, where the contribution of the series resistances (such as the contact resistance Rc and the access resistance Racc) are still included. A more refined calculation of the graphene field effect mobility would include the elimination of the series resistance contributions in order to extract the intrinsic transfer conductance and the related mobility.

Significant improvements in the transfer conductance and mobility of large area Gr-FETs on flexible substrates will be expected by the use polymeric substrates with optimized lower roughness and by further improvements in the graphene transferring methods, e.g., adopting alternative transfer layers different than common PMMA, leaving a very limited amount of chemical residues on graphene [22].

The field effect modulation of the channel conductivity obtained so far using the thin Al2O3 back-gate dielectric make the fabricated Gr-FETs interesting as a platform for chemical sensing applications. In this sense, a key step will be proper functionalization of graphene channel to enhance the sensitivity to specific analytes.

Top

Conclusion

In conclusion, we reported recent advances in the fabrication of Gr-FET with large channel areas (≈104 µm2) and local back-gate on flexible PEN substrates. Particular attention was paid to the fabrication of a thin Al2O3 dielectric film at low temperature. In particular, a low temperature (100 °C) PE-ALD process was optimized and properly tested on a standard substrate (Si) in comparison with a standard PE-ALD deposition. This revealed a material with good morphology, reasonable growth per cycle and comparable dielectric performance. The optimized dielectric material deposition was exploited in order to fabricate back-gated Gr-FETs directly on a PEN substrate, with a gate oxide thickness of 30 nm. Electrical characterization of the Gr-FET devices is reported in order to evaluate key electrical parameters such as the transfer conductance, graphene doping and electron and hole mobility. The fabricated devices will represent the platform for the implementation of solid IS-FETs that can be part of a fully flexible, integrated system for sensing and signal processing.

Top

Acknowledgements

This work has been supported, in part, by European Union Seventh Framework Program under Grant Agreement No. 604391 Graphene Flagship and by MIUR in the framework of the FlagERA project GraNitE.

Top

References

  1. Cheng, I-C.; Wagner, S. Overview of Flexible Electronics Technology. In Flexible Electronics; Wong, W. S.; Salleo, A., Eds.; Electronic Materials: Science & Technology, Vol. 11; Springer: Berlin, Germany, 2009; pp 1–28. doi:10.1007/978-0-387-74363-9_1
    Return to citation in text: [1]
  2. Akinwande, D.; Petrone, N.; Hone, J. Nat. Commun. 2014, 5, 5678. doi:10.1038/ncomms6678
    Return to citation in text: [1]
  3. Kim, D.-H.; Ahn, J.-H.; Choi, W. M.; Kim, H.-S.; Kim, T.-H.; Song, J.; Huang, Y. Y.; Liu, Z.; Lu, C.; Rogers, J. A. Science 2008, 320, 507. doi:10.1126/science.1154367
    Return to citation in text: [1]
  4. Viventi, J.; Kim, D.-H.; Moss, J. D.; Kim, Y.-S.; Justin, J. A.; Annetta, N.; Hicks, A.; Xiao, J.; Huang, Y.; Callans, D. J.; Rogers, J. A.; Litt, B. Sci. Transl. Med. 2010, 2, 24. doi:10.1126/scitranslmed.3000738
    Return to citation in text: [1]
  5. Hwang, S.-W.; Tao, H.; Kim, D.-H.; Cheng, H.; Song, J.-K.; Rill, E.; Brenckle, M. A.; Panilaitis, B.; Won, S. M.; Kim, Y.-S.; Song, Y. M.; Yu, K. J.; Ameen, A.; Li, R.; Su, Y.; Yang, M.; Kaplan, D. L.; Zakin, M. R.; Slepian, M. J.; Huang, Y.; Omenetto, F. G.; Rogers, J. A. Science 2012, 337, 1640. doi:10.1126/science.1226325
    Return to citation in text: [1]
  6. Lee, C.; Wei, X.; Kysar, J. W.; Hone, J. Science 2008, 321, 385. doi:10.1126/science.1157996
    Return to citation in text: [1]
  7. Kim, K. S.; Zhao, Y.; Jang, H.; Lee, S. Y.; Kim, J. M.; Kim, K. S.; Ahn, J.-H.; Kim, P.; Choi, J.-Y.; Hong, B. H. Nature 2009, 457, 706. doi:10.1038/nature07719
    Return to citation in text: [1] [2]
  8. Kwak, B. W.; Choi, Y. C.; Lee, B. S. Phys. E (Amsterdam, Neth.) 2015, 68, 33. doi:10.1016/j.physe.2014.12.017
    Return to citation in text: [1]
  9. Lin, Y.-M.; Dimitrakopoulos, C.; Jenkins, K. A.; Farmer, D. B.; Chiu, H.-Y.; Grill, A.; Avouris, P. Science 2010, 327, 662. doi:10.1126/science.1184289
    Return to citation in text: [1]
  10. Lee, J.; Ha, T.-J.; Li, H.; Parrish, K. N.; Holt, M.; Dodabalapur, A.; Ruoff, R. S.; Akinwande, D. ACS Nano 2013, 7, 7744. doi:10.1021/nn403487y
    Return to citation in text: [1]
  11. Schedin, F.; Geim, A. K.; Morozov, S. V.; Hill, E. W.; Blake, P.; Katsnelson, M. I.; Novoselov, K. S. Nat. Mater. 2007, 6, 652. doi:10.1038/nmat1967
    Return to citation in text: [1]
  12. Pearce, R.; Iakimov, T.; Andersson, M.; Hultman, L.; Lloyd Spetz, A.; Yakimova, R. Sens. Actuators, B 2011, 155, 451. doi:10.1016/j.snb.2010.12.046
    Return to citation in text: [1]
  13. Li, X.; Cai, W.; An, J.; Kim, S.; Nah, J.; Yang, D.; Piner, R.; Velamakanni, A.; Jung, I.; Tutuc, E.; Banerjee, S. K.; Colombo, L.; Ruoff, R. S. Science 2009, 324, 1312. doi:10.1126/science.1171245
    Return to citation in text: [1] [2]
  14. Faggio, G.; Capasso, A.; Messina, G.; Santangelo, S.; Dikonimos, T.; Gagliardi, S.; Giorgi, R.; Morandi, V.; Ortolani, L.; Lisi, N. J. Phys. Chem. C 2013, 117, 21569. doi:10.1021/jp407013y
    Return to citation in text: [1]
  15. Yan, F.; Zhang, M.; Li, J. Adv. Healthcare Mater. 2014, 3, 313. doi:10.1002/adhm.201300221
    Return to citation in text: [1]
  16. Bergveld, P. IEEE Trans. Biomed. Eng. 1970, MBE–17, 70. doi:10.1109/TBME.1970.4502688
    Return to citation in text: [1]
  17. Zhu, Y.; Wang, C.; Petrone, N.; Yu, J.; Nuckolls, C.; Hone, J.; Lin, Q. A solid-gated graphene fet sensor for PH measurements. In 2015 28th IEEE International Conference on Micro Electro Mechanical Systems (MEMS), Estoril, Portugal, Jan 18–22, 2015; IEEE Publishing: Piscataway, NJ, U.S.A., 2015; pp 869 ff. doi:10.1109/memsys.2015.7051097
    Return to citation in text: [1]
  18. Groner, M. D.; Fabreguette, F. H.; Elam, J. W.; George, S. M. Chem. Mater. 2004, 16, 639. doi:10.1021/cm0304546
    Return to citation in text: [1]
  19. Blaho, M.; Gregušová, D.; Jurkovič, M.; Haščík, Š.; Fedor, J.; Kordoš, P.; Fröhlich, K.; Brunner, F.; Cho, M.; Hilt, O.; Würfl, J.; Kuzmík, J. Microelectron. Eng. 2013, 112, 204. doi:10.1016/j.mee.2013.03.120
    Return to citation in text: [1]
  20. Kim, S.; Nah, J.; Jo, I.; Shahrjerdi, D.; Colombo, L.; Yao, Z.; Tutuc, E.; Banerjee, S. K. Appl. Phys. Lett. 2009, 94, 062107. doi:10.1063/1.3077021
    Return to citation in text: [1]
  21. Giannazzo, F.; Sonde, S.; Lo Nigro, R.; Rimini, E.; Raineri, V. Nano Lett. 2011, 11, 4612. doi:10.1021/nl2020922
    Return to citation in text: [1]
  22. Van Ngoc, H.; Qian, Y.; Han, S. K.; Dae, J. K. Sci. Rep. 2016, 6, 33096. doi:10.1038/srep33096
    Return to citation in text: [1]
Top
Figure 1: a) Comparison between tapping mode atomic force microscopy (tAFM) morphologies of low temperature (left) and standard temperature (right) dielectric materials deposited on a Si wafer; b) AFM local step height of the lift-off patterned low temperature dielectric; c) comparison between tAFM morphologies of low temperature (left) and standard temperature (right) dielectric material deposited on an Al coated Si wafer; and d) current density leakage through low temperature and standard temperature dielectric materials. Move  Close
Figure 2: a) Tapping mode atomic force microscopy (tAFM) morphology of the PEN surface and b) a schematic representation of the PEN starting substrate. c) tAFM morphology of the PEN-coated surface by a 100 nm protective Al2O3 layer and d) a schematic representation of the Al2O3 barrier/PEN substrate. Move  Close
Figure 3: a) Tapping mode atomic force microscopy (tAFM) morphology and b) schematic illustration of the aluminum back-gate pad. c) tAFM morphology and d) related schematic illustration of the Al2O3 deposited by the low temperature ALD process. Move  Close
Figure 4: a) Tapping mode atomic force microscopy (tAFM) morphology and b) schematic illustration of the graphene channel. c) Optical microscopy and d) schematic illustration of the final back-gated device with the detail of the involved series resistance contributions from source to drain. Move  Close
Figure 5: a) IdVd characteristics at different back gate bias values and b) IdVg transfer characteristic for a representative Gr-FET with channel width W = 100 μm, channel length L = 190 μm and access regions length Lacc = 20 μm. In the insert of b) the leakage current (Ig vs Vg) collected simultaneously to the transfer characteristic measurement is shown. Move  Close
Figure 6: Transfer conductance, gm, of the Gr-FET, calculated from the Id vs Vg transfer characteristic. Move  Close
Table 1: Comparison between the low temperature and standard temperature process properties extracted during the material characterization on the standard Si substrates. Move  Close
 Low temperature (100 °C)Standard temperature (250 °C)
Growth per Cycle:  
* Ellipsometry0.16 nm/cycle0.12 nm/cycle
* Local step height0.168 nm/cycle
Relative permittivity7.917.95
Leakage (6 MV/cm)6.6 × 10−7 A/cm21.1 × 10−7 A/cm2
Roughness (RMS):  
* On Si wafer0.297 nm0.443 nm
* On sputtered Al4.20 nm4.49 nm
10.Lee, J.; Ha, T.-J.; Li, H.; Parrish, K. N.; Holt, M.; Dodabalapur, A.; Ruoff, R. S.; Akinwande, D. ACS Nano 2013, 7, 7744. doi:10.1021/nn403487y
Go to reference 10
11.Schedin, F.; Geim, A. K.; Morozov, S. V.; Hill, E. W.; Blake, P.; Katsnelson, M. I.; Novoselov, K. S. Nat. Mater. 2007, 6, 652. doi:10.1038/nmat1967
Go to reference 11
7.Kim, K. S.; Zhao, Y.; Jang, H.; Lee, S. Y.; Kim, J. M.; Kim, K. S.; Ahn, J.-H.; Kim, P.; Choi, J.-Y.; Hong, B. H. Nature 2009, 457, 706. doi:10.1038/nature07719
8.Kwak, B. W.; Choi, Y. C.; Lee, B. S. Phys. E (Amsterdam, Neth.) 2015, 68, 33. doi:10.1016/j.physe.2014.12.017
Go to references 7,8
9.Lin, Y.-M.; Dimitrakopoulos, C.; Jenkins, K. A.; Farmer, D. B.; Chiu, H.-Y.; Grill, A.; Avouris, P. Science 2010, 327, 662. doi:10.1126/science.1184289
Go to reference 9
4.Viventi, J.; Kim, D.-H.; Moss, J. D.; Kim, Y.-S.; Justin, J. A.; Annetta, N.; Hicks, A.; Xiao, J.; Huang, Y.; Callans, D. J.; Rogers, J. A.; Litt, B. Sci. Transl. Med. 2010, 2, 24. doi:10.1126/scitranslmed.3000738
5.Hwang, S.-W.; Tao, H.; Kim, D.-H.; Cheng, H.; Song, J.-K.; Rill, E.; Brenckle, M. A.; Panilaitis, B.; Won, S. M.; Kim, Y.-S.; Song, Y. M.; Yu, K. J.; Ameen, A.; Li, R.; Su, Y.; Yang, M.; Kaplan, D. L.; Zakin, M. R.; Slepian, M. J.; Huang, Y.; Omenetto, F. G.; Rogers, J. A. Science 2012, 337, 1640. doi:10.1126/science.1226325
Go to references 4,5
6.Lee, C.; Wei, X.; Kysar, J. W.; Hone, J. Science 2008, 321, 385. doi:10.1126/science.1157996
Go to reference 6
2.Akinwande, D.; Petrone, N.; Hone, J. Nat. Commun. 2014, 5, 5678. doi:10.1038/ncomms6678
Go to reference 2
3.Kim, D.-H.; Ahn, J.-H.; Choi, W. M.; Kim, H.-S.; Kim, T.-H.; Song, J.; Huang, Y. Y.; Liu, Z.; Lu, C.; Rogers, J. A. Science 2008, 320, 507. doi:10.1126/science.1154367
Go to reference 3
1.Cheng, I-C.; Wagner, S. Overview of Flexible Electronics Technology. In Flexible Electronics; Wong, W. S.; Salleo, A., Eds.; Electronic Materials: Science & Technology, Vol. 11; Springer: Berlin, Germany, 2009; pp 1–28. doi:10.1007/978-0-387-74363-9_1
Go to reference 1
13.Li, X.; Cai, W.; An, J.; Kim, S.; Nah, J.; Yang, D.; Piner, R.; Velamakanni, A.; Jung, I.; Tutuc, E.; Banerjee, S. K.; Colombo, L.; Ruoff, R. S. Science 2009, 324, 1312. doi:10.1126/science.1171245
Go to reference 13
19.Blaho, M.; Gregušová, D.; Jurkovič, M.; Haščík, Š.; Fedor, J.; Kordoš, P.; Fröhlich, K.; Brunner, F.; Cho, M.; Hilt, O.; Würfl, J.; Kuzmík, J. Microelectron. Eng. 2013, 112, 204. doi:10.1016/j.mee.2013.03.120
Go to reference 19
18.Groner, M. D.; Fabreguette, F. H.; Elam, J. W.; George, S. M. Chem. Mater. 2004, 16, 639. doi:10.1021/cm0304546
Go to reference 18
14.Faggio, G.; Capasso, A.; Messina, G.; Santangelo, S.; Dikonimos, T.; Gagliardi, S.; Giorgi, R.; Morandi, V.; Ortolani, L.; Lisi, N. J. Phys. Chem. C 2013, 117, 21569. doi:10.1021/jp407013y
Go to reference 14
15.Yan, F.; Zhang, M.; Li, J. Adv. Healthcare Mater. 2014, 3, 313. doi:10.1002/adhm.201300221
Go to reference 15
16.Bergveld, P. IEEE Trans. Biomed. Eng. 1970, MBE–17, 70. doi:10.1109/TBME.1970.4502688
Go to reference 16
17.Zhu, Y.; Wang, C.; Petrone, N.; Yu, J.; Nuckolls, C.; Hone, J.; Lin, Q. A solid-gated graphene fet sensor for PH measurements. In 2015 28th IEEE International Conference on Micro Electro Mechanical Systems (MEMS), Estoril, Portugal, Jan 18–22, 2015; IEEE Publishing: Piscataway, NJ, U.S.A., 2015; pp 869 ff. doi:10.1109/memsys.2015.7051097
Go to reference 17
22.Van Ngoc, H.; Qian, Y.; Han, S. K.; Dae, J. K. Sci. Rep. 2016, 6, 33096. doi:10.1038/srep33096
Go to reference 22
12.Pearce, R.; Iakimov, T.; Andersson, M.; Hultman, L.; Lloyd Spetz, A.; Yakimova, R. Sens. Actuators, B 2011, 155, 451. doi:10.1016/j.snb.2010.12.046
Go to reference 12
20.Kim, S.; Nah, J.; Jo, I.; Shahrjerdi, D.; Colombo, L.; Yao, Z.; Tutuc, E.; Banerjee, S. K. Appl. Phys. Lett. 2009, 94, 062107. doi:10.1063/1.3077021
Go to reference 20
7.Kim, K. S.; Zhao, Y.; Jang, H.; Lee, S. Y.; Kim, J. M.; Kim, K. S.; Ahn, J.-H.; Kim, P.; Choi, J.-Y.; Hong, B. H. Nature 2009, 457, 706. doi:10.1038/nature07719
Go to reference 7
21.Giannazzo, F.; Sonde, S.; Lo Nigro, R.; Rimini, E.; Raineri, V. Nano Lett. 2011, 11, 4612. doi:10.1021/nl2020922
Go to reference 21
13.Li, X.; Cai, W.; An, J.; Kim, S.; Nah, J.; Yang, D.; Piner, R.; Velamakanni, A.; Jung, I.; Tutuc, E.; Banerjee, S. K.; Colombo, L.; Ruoff, R. S. Science 2009, 324, 1312. doi:10.1126/science.1171245
Go to reference 13
© 2017 Fisichella et al.; licensee Beilstein-Institut.
This is an Open Access article under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
The license is subject to the Beilstein Journal of Nanotechnology terms and conditions: (http://www.beilstein-journals.org/bjnano)