1 article(s) from Gapska, Anna
Scheme of the formation of the gold nanoislands.
Jump to Figure 1
SEM images of 2.8 nm Au films on a Si(111) substrate: a) as prepared, annealed at b) 150 °C, c) 200...
Jump to Figure 2
SEM images of 2.8 nm Au films on a Si(111) substrate annealed at a) 450 °C, b) 550 °C, c) 600 °C fo...
Jump to Figure 3
SEM images of Au films of different thicknesses on a Si(111) substrate annealed at 550 °C for 15 mi...
Jump to Figure 4
a) Number of nanoparticles and b) average diameter of nanoparticles as function of the Au film thic...
Jump to Figure 5
Left: AFM image of a 2.8 nm Au film on a Si(111) substrate annealed at 550 °C for 15 min; right: cr...
Jump to Figure 6
XRD result of a 2.8 nm Au film annealed at 550 °C for 15 min and an as-prepared 2.8 nm Au film on S...
Jump to Figure 7
XPS (Au region) results for the 2.8 nm Au thin film on a Si(111) substrate annealed at 550 °C for 1...
Jump to Figure 8
XPS result (Si region) for the 2.8 nm Au film on a Si(111) substrate annealed at 550 °C for 15 min.
Jump to Figure 9
Absorbance spectra recorded for a 2.8 nm Au film on a Si(111) substrate annealed at 550 °C for 15 m...
Jump to Figure 10
SEM image of the gold nanoislands on the silicon substrate (sample 2.8 nm Au film on Si(111) substr...
Jump to Figure 11
Setup for the FDTD and FDTD/DFT simulations. Left: view from the bottom, zx-plane; yellow rectangle...
Jump to Figure 12
Calculated intensity distribution of the electromagnetic field with unpolarized incident light of a...
Jump to Figure 13
Calculated amplitudes of the components of the electromagnetic field with unpolarized incident ligh...
Jump to Figure 14
Calculated absorbance (as log(Io/Ir), where Io is an incident flux, and Ir – reflected flux), as th...
Jump to Figure 15
Beilstein J. Nanotechnol. 2018, 9, 2599–2608, doi:10.3762/bjnano.9.241