Controlled synthesis of poly(3-hexylthiophene) in continuous flow

There is an increasing demand for organic semiconducting materials with the emergence of organic electronic devices. In particular, large-area devices such as organic thin-film photovoltaics will require significant quantities of materials for device optimization, lifetime testing and commercialization. Sourcing large quantities of materials required for the optimization of large area devices is costly and often impossible to achieve. Continuous-flow synthesis enables straight-forward scale-up of materials compared to conventional batch reactions. In this study, poly(3-hexylthiophene), P3HT, was synthesized in a bench-top continuous-flow reactor. Precise control of the molecular weight was demonstrated for the first time in flow for conjugated polymers by accurate addition of catalyst to the monomer solution. The P3HT samples synthesized in flow showed comparable performance to commercial P3HT samples in bulk heterojunction solar cell devices.


Introduction
Poly(3-hexylthiophene), P3HT, is the most investigated material in bulk heterojunction (BHJ) organic solar cells (OSC) [1]. The reasons for its dominance in the field include its simple chemical structure, controlled synthetic method, reasonable spectral absorption, good semiconducting properties, high chemical stability, and wide commercial availability. Its emergence as a semiconducting material came with the development of synthetic methods that enable production of highly regioregular P3HT with good control of the molecular weight [2,3]. Currently, the preferred method for the synthesis of regioreg-ular P3HT is the Kumada catalyst transfer polymerization (KCTP) or also referred to as Grignard metathesis polymerization (GRIM) [4,5]. This method is attractive because of readily available reagents, relatively mild reaction conditions, and short polymerization time. In the most basic reaction setup, 2,5dibromo-3-hexylthiophene is treated with one equivalent of alkylmagnesium chloride to form a mixture of monosubstituted thiophene Grignard monomers (Scheme 1a). On addition of a desired amount of Ni(II) catalyst, the active catalyst species is formed in solution, and polymerization proceeds until all of the reactive Grignard monomer has been consumed. Controlled polymerization and high molecular weights have been demonstrated by many research groups with variations to this general method [6][7][8][9].
Significant quantities of materials are required for the optimization of large-area roll-to-roll printed organic solar cells [3,10]. While some of the organic semiconducting materials can be obtained commercially an a hundreds-of-grams scale, it is important to explore methods for scaled-up production in order to gain access to in-house materials at reasonable costs and lead times. In addition, batch-to-batch variations in the molecular weight distribution have been observed in commercial polymer samples, leading to differences in material deposition and film quality. This will almost certainly create problems with the performance consistency of large-area roll-to-roll printed devices. To this end, we have started to examine some key reactions in the synthesis of organic electronic materials using continuous-flow processing [11][12][13].
Continuous-flow synthesis methods offer several advantages over traditional batch methods [14][15][16][17][18]. The scale-up of reactions is not only straightforward in continuous processing, but there are also benefits in high reaction reproducibility through  [11] as well as rapid conjugated-polymer synthesis using Suzuki-Miyaura and Stille coupling [12]. In this study, the continuous-flow synthesis of P3HT is examined. Distinct from a recent report of P3HT synthesis in a droplet-based microreactor [20], development of the flow synthesis is described in detail and controlled polymerization of P3HT, both in terms of molecular weight and regioregularity, has been achieved in this work. In particular, the feed ratio of catalyst to monomer was accurately controlled giving polymers with molecular weights ranging from 5 to 40 kg/mol as desired. In addition, BHJ devices prepared using commercial, batch and flow-synthesized P3HT gave comparable performance.

Results and Discussion
The most widely used synthetic route to regioregular P3HT is the Kumada catalyst transfer polycondensation (KCTP) developed by the McCullough group [6] and the Yokozawa group [7]. In a representative experiment for the preparation of P3HT, the thiophene Grignard monomer 2 is prepared from the magnesium exchange reaction of an alkyl Grignard reagent and 2,5dibromo-3-hexylthiophene (1, Scheme 1a). It should be noted here that a mixture of Grignard monomers 2a and 2b is produced in this step, typically in a ratio of 75:25. Only 2a participates in the polymerization step on addition of the catalyst, Ni(dppp)Cl 2 , as a solid (Scheme 1a) [6]. As KCTP is a quasi-living polymerization, the product molecular weight can be controlled by adjusting the monomer-to-catalyst ratio [21].
At the start of this study, the aim was to transfer conventional batch reaction conditions for P3HT synthesis to continuousflow processing. The polymerization step in flow was examined first with the thiophene Grignard monomer prepared in batch. Good solubility and solvent compatibility in the polymer-ization are essential factors to be evaluated for the translation into flow methods. The accurate addition of Ni catalyst to the thiophene Grignard monomer results in the desired catalyst-tomonomer ratio and molecular-weight control. An initial attempt was made to prepare a solution of the commonly used Ni(dppp)Cl 2 catalyst in tetrahydrofuran (THF) which was then added to a solution of the thiophene Grignard monomer. Two problems immediately arose from this early experiment. The Ni(dppp)Cl 2 catalyst only has modest solubility in THF at room temperature. This limited the concentration of the polymerization reaction. The second more serious problem is the dissociation of the catalyst species in THF solution. There was a visible color change in the Ni(dppp)Cl 2 /THF solution from orange to colorless over a period of several minutes. The dissociation of the catalyst species was accompanied by a decrease in catalyst activity leading to low polymer formation. To solve this problem, we were inspired by the work of a number of research groups, in which polymerization was externally initiated from an active tolyl-functionalized nickel complex 3 (Scheme 1a) [8,9,22]. The tolyl-nickel species 3 is soluble and shows good stability in THF in an inert environment. Further, polymers initiated with this complex showed lower defect levels [23,24]. After successfully experimenting with this catalyst in batch conditions, the reagent was applied in flow processing for the synthesis of P3HT (Scheme 1b).
The thiophene Grignard reagent 2 was prepared by traditional batch chemistry and the conversion and regioisomeric ratio were assessed in quenching experiments (Scheme 1a, ratio 2a to 2b 77:23; see Figure S2 in Supporting Information File 1 for 1 H NMR data). The Ni catalyst 3 was delivered to a T-piece via an injection loop and mixed with a stream of Grignard 2 (Scheme 1b) [25]. The mixture was directed to a preheated coil reactor (polyfluoroalkoxy, PFA) at 100 °C with a retention time of 30 min. The polymer solution was then quenched in methanolic HCl (2 M) and the precipitated product was collected. The monomer-to-initiator ratio was adjusted through the variation of flow rates and reagent concentrations (Table 1). Gel-permeation chromatography (GPC) analysis in toluene (against polystyrene standards) revealed the formation of polymer with number-average molecular weights (M n ) ranging from 5 to 40 kg/mol. The M n values increased linearly with nickel catalyst content, providing evidence for the quasi-living nature [21] of the polymerization in flow processing (Table 1 and Figure 1). In fact, the molecular-weight data obtained in conventional batch reactions were very similar to those recorded in continuous-flow reactions ( Figure 1). Matrix-assisted laser desorption ionization mass spectrometry (MALDIMS) and 1 H NMR experiments were used to determine the degree of end-group control in these polymerizations [8,26]. From the mass of the polymeric species and the distinctive proton resonance of the end-groups, it was possible to detect the presence of o-tolyl/H, H/H and Br/H end-groups ( Figure 2 and Supporting Information File 1 for details). As Ni catalyst 3 was prepared from Ni(dppp)Cl 2 and used directly in the polymerization, the formation of different end-group species can be attributed to polymer initiation by residual Ni(dppp)Cl 2 species [24].
While Ni catalyst 3 successfully initiated polymerizations in the time frame of this experiment, it lacked the long term stability in solution required for potential large-scale flow production of  Table 1 for experimental data).
P3HT. An alternative approach was to dissolve Ni(dppp)Cl 2 in a solvent system that limited the ligand-dissociation phenomenon observed in THF. After the screening of a number of organic solvents, Ni(dppp)Cl 2 was found to be soluble in o-dichlorobenzene (o-DCB) and showed good stability with catalytic activity maintained over several days under normal atmospheric conditions. It is interesting to note that o-DCB did not adversely affect the polymerization in batch reactions despite the possibility that the aryl chloride solvent might participate in the Kumada reaction. Apparently, the reactivity of aryl chloride is significantly lower than that of aryl bromide under these reaction conditions.
With  (Figure 3). As our current flow setup is limited by the size of the coil reactors, we anticipate that larger coil reactor volumes would ensure high-throughput production of high-molecular-weight P3HT in continuous flow.
In our studies, stainless-steel tube reactors were also examined for the synthesis of P3HT. In comparison to polyfluoroalkoxy (PFA) tube reactors, stainless-steel tube reactors offer the advantage of low gas permeability. Satisfactory results were  Table 2 for experimental data).
achieved for relatively low degrees of polymerization in the stainless-steel reactors ( Table 2, entries 1 and 2). Interestingly, higher molecular weights could only be achieved in the PFA reactors ( Table 2, entries [3][4][5]. This suggests that the nickelcatalyzed polymerization is incompatible with the stainless-steel reactor and we speculate that the nickel content in stainless steel may be the cause of the incompatibility especially at the elevated reaction temperatures used. To demonstrate the flow synthesis of P3HT from 2,5-dibromo-3-hexylthiophene (1), the Grignard metathesis step was performed in the tube reactor followed by the addition of the Ni(dppp)Cl 2 catalyst for the polymerization (Scheme 2). In this telescoped process, the thiophene Grignard compounds 2a and 2b were formed in the first coil and subsequently mixed with the catalyst stream and fed into the second reactor (Scheme 2). The two-step reaction was performed under superheated conditions (at 250 psi back pressure) and the reagent flow rates were adjusted to deliver reasonable reaction times for both reactors. For the Grignard metathesis step, a stock solution containing Scheme 2: Schematic representation of the telescoped preparation of P3HT in a flow reactor.   Under these conditions, we succeeded in obtaining P3HT with M n of 31 kg/mol and polydispersity of 1.5 (Table 3, entry 1).
The regioregularity was estimated to be 95% from the integration of the α-methylene protons in the 1 H NMR spectrum ( Figure 4). The same degree of regioregularity was observed for a batch sample of similar molecular weight. Additionally, the variation of the molecular weight was investigated when the [M] 0 /[I] 0 ratio was varied. As expected, increasing the concentration or the flow rate of the catalyst stock solution, afforded lower-molecular-weight polymers ( Table 3, entries 2 and 3). In order to assess the device performance of P3HT synthesized using flow methods described in this study, bulk heterojunction (BHJ) solar cells were fabricated and tested. BHJ devices were fabricated with the following device geometry: The current-density-voltage (J-V) curves for the solar-cell devices prepared from various P3HT samples are shown in Figure 5b. The device performance parameters for the different P3HT samples were all rather similar with power conversion efficiency (PCE) ranging from 2.1 to 2.6% ( Table 4). The short circuit current density (J sc ) parameter showed the largest variations and this directly correlated with the thickness of the device active layer (Table 4). Thinner active layers absorbed less of the incoming irradiation leading to decreased J sc . It is pleasing to note that the performance of the commercial P3HT sample (Merck lisicon SP001) was comparable to that of P3HT from flow synthesis (Table 4). It should be noted that the lower PCE of these devices compared with some literature values [1] was attributed to the fact that all devices were fabricated and measured in air. Interestingly, P3HT samples with different end-group variations did not have significant effects on device performance. These results are extremely encouraging for the product of device-grade P3HT using continuous-flow methods with simple benchtop equipment.

Conclusion
P3HT has been successfully synthesized in continuous flow by using a commercially available benchtop flow reactor. After optimization of reaction conditions, good molecular-weight control was achieved by adjusting the monomer-to-catalyst ratio with variations in reagent concentration and flow rates. This  methodology enables the controlled synthesis of conjugated polymers in flow exclusively by the adjustment of the feed of monomer and initiator into the tube reactor. The major challenge in this study was to find compatible nickel catalyst systems for the Kumada polymerization step in flow. Both o-tolyl-Ni catalyst 3 in THF and Ni(dppp)Cl 2 in o-DCB were highly active in continuous processing conditions, and highmolecular-weight P3HT was obtained for both catalysts. Apart from the molecular weight of the polymers, the P3HT samples synthesized in flow showed comparable regioregularity to samples from batch synthesis. The telescoped flow synthesis of P3HT from 2,5-dibromo-3-hexylthiophene (1) was also achieved on the benchtop flow reactor. Finally, BHJ solar cells containing flow-synthesized P3HT showed comparable performance to both commercial and batch-synthesized samples. This study paves the way for the continuous-flow synthesis of other polymers using the KCTP method. With efficient synthesis of polymers possible in a benchtop flow reactor, scale-up of such materials will become straight forward leading to reduction in production costs and improvements in reproducibility.

Experimental
General: The continuous-flow experiments were conducted by using a Vapourtec R2/R4 unit with multiple perfluoroalkoxy PFA (10 mL internal volume) or stainless steel (10 mL internal volume) reactors connected in series. All solvents were degassed and reactions were performed under anaerobic conditions. The reactants were channelled into the tube reactor by pumping solvent from a reservoir. Residence times in the reactor coils were defined by the flow rate and the volume of the reactor. The system was thoroughly dried by first flushing with anhydrous methanol followed by dried acetone before refilling with anhydrous reaction solvent. Reported yields do not account for axial dispersion of the reaction mixture and the formation of the regioisomer 2b. Gel permeation chromatography (GPC) data was obtained by using toluene as the eluent and calibrated against polystyrene reference standards.
Flow synthesis of P3HT via external initiation with nickel catalyst 3: Stock solutions containing 2-bromo-5-chloromagnesium-3-hexylthiophene (2) (0.35/0.2 M) and Ni(dppp)(o-tolyl)Cl 3 (20/10 mM) were pumped into the PFA coil reactor (3 × 10 mL, 100 °C) at specific flow rates (see Table 1).  (2) and Ni(dppp)Cl 2 (8.8 mM) were pumped into the PFA coil reactor (3 × 10 mL, 100 °C, PFA) or into the stainless steel (SS) reactor (40 mL, 100 °C) at specific flow rates (see Table 2). The variation of the concentration of the thiophene monomer and adjusting of the flow rates afforded five different monomer-to-initiator ratios (2.9, 1.7, 0.9, 0.7, 0.25 catalyst mol %). The stream outlet was fitted with an 8 bar back-pressure regulator. The reaction mixtures were quenched by direct precipitation of the stream leaving the reactor, from methanolic HCl (2 M). The polymers were centrifugated and washed with the same solvent three times. The lower molecular weight sample was then washed with acetone, whereas the rest of the samples were washed with petroleum spirits 40-60 °C. Yield (M n 5.9 kg/mol): 32 mg, 65%. 1  Telescoped preparation of P3HT: A stock solution containing 2,5-dibromo-3-hexylthiophene (0.2 M, THF) and tert-butylmagnesium chloride (1 equiv) was pumped into the PFA coil reactor (2 × 10 mL, 100 °C) at 1 mL/min flow rate, resulting in 20 min residence time. The solution was then mixed with a second stream containing Ni(dppp)Cl 2 catalyst (2.7 mM) at 0.1 mL/min to give a 0.1 mol % catalyst content and directed into a series of two reactors (at 100 °C or/and 150 °C). The inner pressure of the system was adjusted to give a continuous steady flow using a 250 psi back-pressure regulator located at the outlet of the system. The mixture was quenched into methanol, centrifuged and washed with the same solvent three times. The concentrations of the catalyst and flow rates were varied to adjust the monomer-to-initiator ratio (see Table 3). The polymer was subjected to Soxhlet extraction with methanol and petroleum

Supporting Information
Supporting Information File 1 Synthetic procedures for batch reactions, characterization of P3HT samples including NMR and MALDI-TOF spectra, and procedures for device preparation.