1 article(s) from Fauth, Kai
(a) XRD of Pt films on STO(100) and MgO(100) in Bragg–Brentano geometry. The diffractograms clearly...
Jump to Figure 1
SEM images of Co NPs on Pt(111)/MgO(100) and Pt(100)/STO(100) are displayed in panels (a) and (b), ...
Jump to Figure 2
AFM height distributions of Co NPs on Pt(111)/MgO(100) in the as-prepared state and after annealing...
Jump to Figure 3
Panel (a) shows XMCD difference spectra for Co NPs on Pt(111) in the as-prepared state and after an...
Jump to Figure 4
Element specific XMCD hysteresis loops measured at the Co L3 maximum dichroic signal at T = 12 K an...
Jump to Figure 5
(a) In-plane hysteresis loops measured by SQUID magnetometry at T = 29 K, i.e., close to the compen...
Jump to Figure 6
Bright field TEM images of Co NPs on Pt(100) films after annealing at TA = 250 °C (as-prepared stat...
Jump to Figure 7
HRTEM image of annealed Co NPs on Pt(100) film after TA = 500 °C for 30 min. The arrows indicate a ...
Jump to Figure 8
The left image shows the high angle annular dark-field (HAADF) image of the sample shown in Figure 8 using ...
Jump to Figure 9
Proposed model of local alloying and diffusion of Co NPs on Pt films. Details are discussed in the ...
Jump to Figure 10
Beilstein J. Nanotechnol. 2011, 2, 473–485, doi:10.3762/bjnano.2.51