2 article(s) from Herrmann, Rudolf
- Review
- Published 16 Dec 2014
-
PDF -
Album-
![]()
Figure 1: Fluorescent dyes used for labelling.
-
![]()
Figure 2: Fluorescence emission spectra in ethanol of MPD (excitation 488 nm, left) and ATTO 647N-APS (excita...
-
![]()
Figure 3: Scattering corrections to the experimental absorption spectra of labelled NP dispersions in ethanol...
-
![]()
Figure 4: Left: TEM image of core-shell NP with secondary SiO2 layer. Average diameter: 31 ± 11 nm, with a co...
-
![]()
Figure 5: TEM images of CeO2 NP prepared according to [43]. Left: solvent ethanol/water 4:1, spherical particles,...
-
![]()
Figure 6: TEM images of agglomerates of CeO2 NP prepared according to [48], with average diameter of the circumsc...
-
![]()
Figure 7: STEM image (left) and EDX mapping (right) of agglomerates of Pt-decorated CeO2 NP (diameter of the ...
-
![]()
Figure 8: STEM image (left) and EDX mapping (right) of agglomerates of Pd-decorated CeO2 NP (diameter of the ...
-
- Full Research Paper
- Published 05 Nov 2014
-
PDF -
Album-
![]()
Figure 1: Left: ZnO-NP prepared by the acidic procedure (sample 1, without labelling; scale bar: 50 nm). Righ...
-
![]()
Figure 2: TEM pictures of ZnO-NP 1 (labeled with a perylene dye) as prepared (left) and after one hour of rea...
-
![]()
Figure 3: Left: TEM picture of degraded ZnO-NP 2 (labelled) after 1 hour of reaction with buffer B. The scale...
-
![]()
Figure 4: Commercial ZnO sample 3 after treatment with buffer B (2000 mg/L) for one hour. The general appeara...
-
![]()
Figure 5: SiO2-coated labelled ZnO-NP (sample 4; shell thickness 3–6 nm) before (left; scale bar 20 nm) and a...
-