2 article(s) from Pereira, Alejandro
Three-step scheme to synthesize titanium dioxide nanospheres from electrosprayed SPVP spherical par...
Jump to Figure 1
Photographs of: (a) electrosprayed spherical PVP particles (SPVP); (b) deposition of Al2O3 on SPVP ...
Jump to Figure 2
TEM images of calcined nanospheres, CSTiO2, at: (a) 2000×; (b) 5000×; (c) 10000× and (d) further de...
Jump to Figure 3
(a) EDX mapping marked with red (oxygen), green (aluminum) and yellow (titanium), (b) EDX spectrum ...
Jump to Figure 4
XRD diffraction patterns of: PVP electrosprayed spheres (SPVP), double coated spheres (SPVP_Al2O3_T...
Jump to Figure 5
The I(q)–q plot of CSTiO2 structures obtained by SAXS.
Jump to Figure 6
Beilstein J. Nanotechnol. 2019, 10, 1716–1725, doi:10.3762/bjnano.10.167
Outline of the AFIR process. Si(100) wafers with a native layer of SiO2 were coated with Fe2O3. Ant...
(a) SEM image of the antidot array patterned on the film with 27 nm thickness. (b) Profile obtained...
XRD patterns of the as-deposited Fe2O3 film (blue curve) and the Fe3O4 film (red curve) after the t...
Central region of the hysteresis curves for the antidot arrays obtained from a 27 nm thick film. (a...
(a) Coercivity of the initial thin film and of the square (blue squares) and the hexagonal (red tri...
Coercivity (red squares) and normalized remanence (blue dots) as a function of the angle θ at which...
Beilstein J. Nanotechnol. 2018, 9, 1728–1734, doi:10.3762/bjnano.9.164