2 article(s) from Reckinger, Nicolas
(a–c) Typical field-emission SEM images with different magnifications of MoS2 NSs grown by double s...
Jump to Figure 1
MoS2 NSs grown by double sulfurization of a 50 nm Mo film at 850 °C on SiO2/Si substrates: (a) typi...
Jump to Figure 2
MoS2 sample grown by double sulfurization of a 50 nm Mo film at 850 °C on SiO2/Si substrates: (a) P...
Jump to Figure 3
MoS2 sample grown by double sulfurization of a 50 nm Mo film at 850 °C on SiO2/Si substrates: (a) H...
Jump to Figure 4
Photographs of (a) wet chemically transferred MoS2 sample on the FTO/glass substrate, the FTO film ...
Jump to Figure 5
(a) Field-emission current density as a function of the electric field for the transferred MoS2 NSs...
Jump to Figure 6
Beilstein J. Nanotechnol. 2018, 9, 1686–1694, doi:10.3762/bjnano.9.160
FE-SEM images of sensor devices made of VA-CNTs decorated with gold nanoparticles with different CN...
(a) Top and (b) side SEM views of the VA-CNTs.
High resolution TEM images of the carbon nanotubes constituting the forests.
Typical Raman spectrum of VA-CNT sensors.
TEM images of VA-CNTs decorated with gold nanoparticles.
XPS survey spectra for pristine VA-CNTs (top, black line) and 150 µm-long VA-CNTs decorated with 6 ...
XPS core level spectra of C 1s (a) and Au 4f (b) recorded on 150 µm-long VA-CNTs decorated with 6 n...
Jump to Figure 7
Room temperature detection of NO2 for sensors with different CNT lengths. White pulses indicate the...
Jump to Figure 8