1 article(s) from Wenzel, Marianne
One of the polymorphs of the microporous ETS-10 consisting of TiO6 octahedra and SiO4 tetrahedra sh...
Jump to Figure 1
X-ray diffractograms of the as-synthesized ETS-10 material (Na,K-ETS-10, top) and of the reference ...
Jump to Figure 2
SEM micrographs of selected crystals representing different types of phases formed during the synth...
Jump to Figure 3
Nitrogen adsorption (solid circles) and desorption (open circles) isotherms of the as-synthesized N...
Jump to Figure 4
Hg intrusion data of the as-synthesized Na,K-ETS-10 material.
Jump to Figure 5
TEM micrographs for the Na,K-ETS-10 material obtained with different magnifications demonstrating a...
Jump to Figure 6
(A) XRD data of post-synthetically treated titanosilicates. The calculated crystallinity decreased ...
Jump to Figure 7
SEM micrographs of the titanosilicates treated with H2O2 for 30, 45 and 60 min (P-ETS-10/30, P-ETS-...
Jump to Figure 8
(A) Nitrogen adsorption and desorption isotherms of titanosilicates treated with H2O2 for 30 min (l...
Jump to Figure 9
TEM images of the selected crystals of P-ETS-10/60 and C-P-ETS 10/60 demonstrating the presence of ...
Jump to Figure 10
Differential thermal analysis of the Na,K-ETS-10 (red), P-ETS-10/60 (blue) and C-P-ETS-10/60 (green...
Jump to Figure 11
Temperature-programmed desorption of NH3 (A) and CO2 (B) in Na,K-ETS-10 (red), P-ETS-10/60 (blue) a...
Jump to Figure 12
The HPDEC (A) and CP (B) 29Si MAS NMR spectra obtained for Na,K-ETS-10 (red), P-ETS-10/60 (blue) an...
Jump to Figure 13
The EPR spectra measured with Na,K-ETS-10 (red), P-ETS-10/60 (blue) and C-P-ETS-10/60 (green) at 70...
Jump to Figure 14
Variable temperature HP 129Xe NMR spectra acquired on Na,K-ETS-10 (A, red), P-ETS-10/60 (B, blue) a...
Jump to Figure 15
1H PFG NMR diffusion attenuation curves of bulk triolein (dashed line) and triolein in oversaturate...
Jump to Figure 16
Schematic representation of the diffusion modes denoted as 1, 2 and 3 in the Figure 16 as observed by PFG NM...
Jump to Figure 17
Conversion of triolein over CaO- (A) and ETS-10-based (B) catalysts at 403 K measured for different...
Jump to Figure 18
Beilstein J. Nanotechnol. 2019, 10, 2039–2061, doi:10.3762/bjnano.10.200