1 article(s) from Wulf, Verena
SEM images of NWs grown on gold-sputtered Si exposed to NPS vapor at 375 °C for 1 h (left: sid...
Jump to Figure 1
Analysis of NWs grown on gold-sputtered Si for 1 h at 375 °C. Top left: Backscattered-electron...
Jump to Figure 2
TEM images of NWs grown on gold-sputtered Si for 1 h at 375 °C. The FFT of the HRTEM image and...
Jump to Figure 3
SEM images of NWs grown on gold-sputtered Si by exposure to NPS vapor for 1 h at 650 °C.
Jump to Figure 4
SEM image of gold nanoparticles formed on the native oxide surface of Si after annealing of Au...
Jump to Figure 5
SEM image of NWs grown at 650 °C for 1 h on Si surfaces with annealed gold films (left: sample...
Jump to Figure 6
SEM image of NWs grown at 375 °C for 1 h, on annealed gold films of different sputtering times (lef...
Jump to Figure 7
SEM image of the chemisorbed gold nanoparticles on the aminopropylated Si surface.
Jump to Figure 8
SEM image of NWs grown from nanoparticles at 650 °C without prior treatment (left) and at 375 °C af...
Jump to Figure 9
SEM images with different magnifications of a spin coated film of “liquid bright gold” on Si a...
Jump to Figure 10
SEM image of Si NWs obtained from spin-coated “liquid bright gold” films after annealing at 650 °C,...
Jump to Figure 11
Optical microscopy images of the different steps of the irradiation-induced pattern formation. Left...
Jump to Figure 12
SEM images (different magnifications) of Si NWs obtained from UV-patterned spin-coated “liquid brig...
Jump to Figure 13
SEM image of the border region of a Si NW pattern obtained from UV-patterned “liquid bright gold” f...
Jump to Figure 14
Beilstein J. Nanotechnol. 2012, 3, 535–545, doi:10.3762/bjnano.3.62