1 article(s) from Yanushkevich, Kazimir I
SEM top view of the obtained porous alumina oxide at different magnification a) 20000×, b) 100000×.
Jump to Figure 1
Deposited mass of Ni and of Ni–Fe as a function of the deposition time. Alumina thickness (HPA) is ...
Jump to Figure 2
SEM cross-sectional views of the alumina template after galvanostatic dc deposition of Ni–Fe (a, b,...
Jump to Figure 3
XRD pattern for Ni NWs in alumina template with HPA of 65 μm and a current density of 3 mA·cm−2, de...
Jump to Figure 4
XRD pattern of Ni–Fe NWs inside the alumina template with HPA of 50 μm and a current density 3 mA·cm...
Jump to Figure 5
Magnetization as a function of the temperature for Ni NWs fabricated in the alumina template (HPA =...
Jump to Figure 6
Magnetization as a function of the temperature for Ni–Fe NWs fabricated in the alumina template (a)...
Jump to Figure 7
Beilstein J. Nanotechnol. 2016, 7, 1709–1717, doi:10.3762/bjnano.7.163