Beilstein J. Nanotechnol. 2016, 7, 591–604, doi:10.3762/bjnano.7.52
Figure 1: Cross-section HRTEM images of small (2–3 nm) FePt NPs on a MgO(001) substrate after annealing at 65...
Figure 2: 3 nm thick FePt film on SiO2/Si(001) substrate after annealing at 650 °C for 30 min: (a) RHEED patt...
Figure 3: Example of an AFM image (left) and height histogram (right) of micellar FePt NPs on SiO2/Si(001) af...
Figure 4: RHEED patterns of 7.6 nm FePt NPs on SiO2/Si(001) after different annealing steps (a) 570 °C for 60...
Figure 5: (a–c) RHEED patterns of a FePt film on Al2O3(0001), recorded with an electron beam energy of 25 keV...
Figure 6: RHEED images of FePt NPs on sapphire(0001) single crystals after several annealing steps, recorded ...
Figure 7: (a–d) RHEED pattern of a FePt film on MgO(100), recorded with an electron beam energy of 25 keV aft...
Figure 8: (a–c) RHEED patterns of large (5–6 nm) FePt nanoparticles prepared on MgO(001), recorded with an el...
Figure 9: RHEED pattern of 2–3 nm FePt particles on MgO(001), recorded with an beam energy of 25 keV after an...
Figure 10: AFM image and height histogram of 2–3 nm FePt nanoparticles on MgO(001) after annealing at 650 °C f...