1 article(s) from Cristiano, Filadelfo
Removed SiGe thickness measured by different methods (TEM, XRD and ellipsometry) as a function of t...
Jump to Figure 1
Removed SiGe thickness (measured by ellipsometry) as a function of etching time for two different G...
Jump to Figure 2
(a) Sheet resistance RS, (b) Hall dose NH, and (c) Hall mobility µH as functions of the etching tim...
Jump to Figure 3
Depth profiles of (a) active dopant concentration and (b) carrier mobility extracted from the DHE m...
Jump to Figure 4
Sheet resistance as a function of the laser energy density for 6 nm SiGeOI (xGe = 0.25) layer impla...
Jump to Figure 5
Hall effect measurements (raw data: (a) RS, (b) NH and (c) µH) of the SiGeOI sample (xGe = 0.25) im...
Jump to Figure 6
Depth profiles of (a) active dopant concentration and (b) carrier mobility extracted from DHE measu...
Jump to Figure 7
Concentration depth profiles of (a) arsenic and (b) oxygen measured by SIMS in 11 nm thick SOI wafe...
Jump to Figure 8
Hall effect measurements (raw data: (a) RS, (b) NH and (c) µH) of the SOI samples implanted with ar...
Jump to Figure 9
Active dopant concentration depth profiles as extracted by DHE measurements from 11 nm thick SOI wa...
Jump to Figure 10
Beilstein J. Nanotechnol. 2018, 9, 1926–1939, doi:10.3762/bjnano.9.184