Long-term stability and scale-up of noncovalently bound gold nanoparticle-siRNA suspensions

• Anna V. Epanchintseva,
• Julia E. Poletaeva,
• Dmitrii V. Pyshnyi,
• Elena I. Ryabchikova and
• Inna A. Pyshnaya

Beilstein J. Nanotechnol. 2019, 10, 2568–2578, doi:10.3762/bjnano.10.248

• siRNA duplex integrity as well as siRNA surface density. Dynamic light scattering, transmission electron microscopy, UV–vis spectroscopy, and electrophoresis were used to study the effect of scaling up the AuNP-siRNA synthesis and long term storage of its suspension on physicochemical properties of the

Advanced hybrid nanomaterials

• Andreas Taubert,
• Fabrice Leroux,
• Pierre Rabu and
• Verónica de Zea Bermudez

Beilstein J. Nanotechnol. 2019, 10, 2563–2567, doi:10.3762/bjnano.10.247

• high UV resistance of polybutylene succinate containing amino-acid-modified layered double hydroxides” [26]. However, this time with a “green aspect”, since the polymer studied is a bio-based polyester and the organo-modifying agent of the 2D-filler is an amino acid. The same host structure (i.e., LDH

Bombesin receptor-targeted liposomes for enhanced delivery to lung cancer cells

• Mohammad J. Akbar,
• Pâmela C. Lukasewicz Ferreira,
• Melania Giorgetti,
• Leanne Stokes and
• Christopher J. Morris

Beilstein J. Nanotechnol. 2019, 10, 2553–2562, doi:10.3762/bjnano.10.246

• were analysed using a gradient elution method using mobile phase A (H2O + 0.1% TFA) and B solution (acetonitrile + 0.1% TFA) on a Perkin Elmer HPLC system comprising of binary solvent pump, autosampler, UV–vis detector and Peltier column oven. Mobile phases were membrane degassed using Millipore vacuum

• mode on a SHIMADZU Axima-CFR MALDI–TOF. Liposomal formulation Lipids for each liposomal formulation were dissolved in chloroform and mixed in a round-bottomed flask (see Table 2, below). The concentration of lipid-PEG-peptide conjugate solutions in chloroform were determined by UV spectroscopy using

Self-assembly of a terbium(III) 1D coordination polymer on mica

• Quentin Evrard,
• Giuseppe Cucinotta,
• Felix Houard,
• Guillaume Calvez,
• Yan Suffren,
• Carole Daiguebonne,
• Olivier Guillou,
• Andrea Caneschi,
• Matteo Mannini and
• Kevin Bernot

Beilstein J. Nanotechnol. 2019, 10, 2440–2448, doi:10.3762/bjnano.10.234

• ]. Moreover, TbIII ions are known to exhibit a strong green luminescence under UV irradiation [14]. Similar to what has been observed for other lanthanide ions, the luminescence emission spectrum is characterized by a line shape that is barely affected by the ionic environment because of the inner nature of

• the 4f orbitals [15]. This emission can be considerably enhanced when the ions are properly coordinated by organic ligands that act as “antennas” for UV irradiation increasing the overall brightness of the compound [14]. In our present work, we have used [Tb(hfac)3·2H2O]n (where hfac

• . Luminescence measurements. Luminescence emission spectra were measured with a Horiba Jobin-Yvon Fluorolog-III fluorescence spectrometer equipped with a 450 W Xe lamp. The emission signal was collected in the 190–860 nm range via a Hamamatsu R928 UV–vis photomultiplier. The sample emission was measured directly

pH-Controlled fluorescence switching in water-dispersed polymer brushes grafted to modified boron nitride nanotubes for cellular imaging

• Saban Kalay,
• Yurij Stetsyshyn,
• Volodymyr Donchak,
• Khrystyna Harhay,
• Ostap Lishchynskyi,
• Halyna Ohar,
• Yuriy Panchenko,
• Stanislav Voronov and
• Mustafa Çulha

Beilstein J. Nanotechnol. 2019, 10, 2428–2439, doi:10.3762/bjnano.10.233

• thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), dynamic light scattering (DLS), ultraviolet–visible spectrophotometry (UV–vis), laser scanning confocal microscopy (LSCM) and scanning electron microscopy (SEM). The DLS results demonstrated that P(AA-co-FA)-functionalized BNNTs

• exhibited good dispersibility in water. pH-Controlled switching of fluorescence was demonstrated using LSCM and UV–vis. In addition, the potential of BNNTs as novel pH-switchable fluorescent water-dispersible materials for cellular imaging has been investigated. The developed hybrid structure can

• the excitation and emission wavelengths were selected at 490 nm and 520 nm, respectively, and the fluorescently labeled nanomaterial was viewed. Ultraviolet–visible spectrometry (UV–vis) The optical absorption spectra of the BNNT suspension were registered on a double-beam UV–vis spectrophotometer

Air oxidation of sulfur mustard gas simulants using a pyrene-based metal–organic framework photocatalyst

• Ghada Ayoub,
• Mihails Arhangelskis,
• Xuan Zhang,
• Florencia Son,
• Timur Islamoglu,
• Tomislav Friščić and
• Omar K. Farha

Beilstein J. Nanotechnol. 2019, 10, 2422–2427, doi:10.3762/bjnano.10.232

• of producing singlet oxygen upon exposure to UV light [44][45], we anticipated that a MOF with isolated pyrene linkers would be a good candidate catalyst for the photocatalytic oxidation of sulfur mustard. The NU-400 material (Figure 1) was synthesized from the pyrene-2,7-dicarboxylic acid (Py-DCA

• –Teller (BET) surface area of 1325 m2/g (Figure S4, Supporting Information File 1) [44]. The pore size analysis using DFT model revealed pores of approximately 11 Å, which is suitable for diffusion of CEES molecules into the pores of NU-400. The solid-state UV–vis spectrum of NU-400 reveals that the

• strongest absorption bands lie below 400 nm (see Figure S5, Supporting Information File 1), leading us to use two commercially available ultraviolet light emitting diodes (UV-LEDs) with λmax = 390–400 nm as a means to excite the MOF for 1O2 production. Results and Discussion As our first entry into

Semitransparent Sb₂S₃ thin film solar cells by ultrasonic spray pyrolysis for use in solar windows

• Jako S. Eensalu,
• Atanas Katerski,
• Erki Kärber,
• Lothar Weinhardt,
• Monika Blum,
• Clemens Heske,
• Wanli Yang,
• Ilona Oja Acik and
• Malle Krunks

Beilstein J. Nanotechnol. 2019, 10, 2396–2409, doi:10.3762/bjnano.10.230

• 600, FEI Company). The optical properties were measured using a UV–vis–NIR spectrophotometer (Jasco V-670, integrating sphere, air reference). The AVT was calculated as the arithmetic average of total transmittance of the glass/ITO/TiO2/Sb2S3 stack in the 380–740 nm wavelength range by using Equation

Deterministic placement of ultra-bright near-infrared color centers in arrays of silicon carbide micropillars

• Stefania Castelletto,
• Abdul Salam Al Atem,
• Faraz Ahmed Inam,
• Hans Jürgen von Bardeleben,
• Sophie Hameau,
• Ahmed Fahad Almutairi,
• Gérard Guillot,
• Shin-ichiro Sato,
• Alberto Boretti and
• Jean Marie Bluet

Beilstein J. Nanotechnol. 2019, 10, 2383–2395, doi:10.3762/bjnano.10.229

• quantum sensing [54] applications using SiC. Experimental Micropillar fabrication and color center generation In this work, micropillars were fabricated by inductively coupled plasma RIE (ICP-RIE) on commercial n-type 4H-SiC. Highly doped n-type 4H-SiC acquired from SiCrystal was used. Using UV laser

• lithography and a metallic hard mask (Ti/Ni), we have realized micropillar arrays with a height of 4.5 µm, a diameter of 700 nm, and a pitch of 4 µm. The fabrication process (Figure 1a–d) started with coating the samples with photoresist (AZ5214E) and exposing them to a UV laser (λ = 365 nm, Heidelberg µPG101

• . In particular N. Terrier for the UV photolithography, R. Mazurczyk for the ICP etching and S. Brottet for SEM imaging. We thank Mr. D. Stavrevski for the technical support with the confocal microscopes at the ARC Centre of Excellence for Nanoscale Biophotonics, School of Applied Science, RMIT

Polyvinylpyrrolidone as additive for perovskite solar cells with water and isopropanol as solvents

• Chen Du,
• Shuo Wang,
• Xu Miao,
• Wenhai Sun,
• Yu Zhu,
• Chengyan Wang and
• Ruixin Ma

Beilstein J. Nanotechnol. 2019, 10, 2374–2382, doi:10.3762/bjnano.10.228

• lead nitrate, to which polyvinylpyrrolidone (PVP) was added in order to enhance the photoelectric performance of the PSCs. By a combination of SEM, EIS, PL and UV spectroscopy and other characterization approaches, we show that the PVP additive is effective in inhibiting carrier recombination

• paper, we describe the preparation of perovskite solar cells from an aqueous solution of lead nitrate as precursor under ambient conditions. In order to improve the photoelectric performance of the PSCs, PVP was added to the precursor solution. A combination of SEM, EIS, PL, UV, and other

• . Device fabrication Prior to spin-coating, the ITO glass substrate was cleaned sequentially with detergent, acetone, ethanol, deionized water, each for 15 min, then dried with a nitrogen flow, and then cleaned with UV/ozone for 20 min. A thin layer of SnO2 nanoparticles was spin-coated on the ITO

Integration of sharp silicon nitride tips into high-speed SU8 cantilevers in a batch fabrication process

• Nahid Hosseini,
• Matthias Neuenschwander,
• Oliver Peric,
• Santiago H. Andany,
• Jonathan D. Adams and
• Georg E. Fantner

Beilstein J. Nanotechnol. 2019, 10, 2357–2363, doi:10.3762/bjnano.10.226

• blunt tips (the tip radius increased by an order of magnitude). Lee et al. have shown that hydrogel AFM cantilevers fabricated by replica moulding and UV curing have great potential for tuning the mechanical properties of the tip, its shape and the surface functionalization [26]. However, the

The role of Ag⁺, Ca²⁺, Pb²⁺ and Al³⁺ adions in the SERS turn-on effect of anionic analytes

• Stefania D. Iancu,
• Andrei Stefancu,
• Vlad Moisoiu,
• Loredana F. Leopold and
• Nicolae Leopold

Beilstein J. Nanotechnol. 2019, 10, 2338–2345, doi:10.3762/bjnano.10.224

• was excluded since no broadening or any additional extinction bands at higher wavelengths were observed in the corresponding UV–vis spectrum (Figure 1B). The incipient dissolution of the AgNPs and the formation of Ag+ ions on the surface of the nanoparticles leads to the adsorption of citrate to the

• exposure each unless otherwise stated. (A) SERS spectra and (B) UV–vis extinction spectra of the colloidal solution of cit-AgNPs at pH values between 4 and 9 as indicated in the figure. SERS spectra of 50 µM organic acids after their addition to cit-AgNPs and after the activation of the AgNPs with 50 µM

Design of a nanostructured mucoadhesive system containing curcumin for buccal application: from physicochemical to biological aspects

• Sabrina Barbosa de Souza Ferreira,
• Gustavo Braga,
• Évelin Lemos Oliveira,
• Jéssica Bassi da Silva,
• Hélen Cássia Rosseto,
• Lidiane Vizioli de Castro Hoshino,
• Mauro Luciano Baesso,
• Wilker Caetano,
• Craig Murdoch,
• Helen Elizabeth Colley and
• Marcos Luciano Bruschi

Beilstein J. Nanotechnol. 2019, 10, 2304–2328, doi:10.3762/bjnano.10.222

• new cases each year worldwide [18][19]. Oral squamous cell carcinoma (OSCC), the primary cause of this cancer type, has been associated with many risk factors, mainly related to excessive intake of alcoholic beverages, tobacco use, high exposure to UV radiation, immunosuppression and age. These risk

Design and facile synthesis of defect-rich C-MoS₂/rGO nanosheets for enhanced lithium–sulfur battery performance

• Chengxiang Tian,
• Juwei Wu,
• Zheng Ma,
• Bo Li,
• Pengcheng Li,
• Xiaotao Zu and
• Xia Xiang

Beilstein J. Nanotechnol. 2019, 10, 2251–2260, doi:10.3762/bjnano.10.217

• (3 mL) as the adsorbents. Ultraviolet–visible (UV–vis) absorption spectra of these diluted solutions were collected using a Shimadzu UV 2550 spectrophotometer. Cell assembly and electrochemical measurements The working electrodes were prepared by casting a slurry of 80 wt % active materials (MoS2-S

• composite renders the Li2S6 solution almost completely colorless while the solution of pristine MoS2 exhibits a stronger coloration than all solutions of C-MoS2/rGO composites. This could be attributed to the porous structure and high specific surface area of the C-MoS2/rGO-6 composite. The UV–vis

• of pristine MoS2, and C-MoS2/rGO and C-MoS2/rGO-6 composites. (c) TG curves of MoS2-S, C-MoS2/rGO-S and C-MoS2/rGO-6-S composites; (d) UV–vis absorption spectra of the pure Li2S6 solution and Li2S6 solutions with pristine MoS2, and C-MoS2/rGO and C-MoS2/rGO-6 composites (inset: photos of the Li2S6

Nontoxic pyrite iron sulfide nanocrystals as second electron acceptor in PTB7:PC₇₁BM-based organic photovoltaic cells

• Olivia Amargós-Reyes,
• José-Luis Maldonado,
• Omar Martínez-Alvarez,
• María-Elena Nicho,
• José Santos-Cruz,
• Juan Nicasio-Collazo,
• Irving Caballero-Quintana and
• Concepción Arenas-Arrocena

Beilstein J. Nanotechnol. 2019, 10, 2238–2250, doi:10.3762/bjnano.10.216

• characteristics could facilitate exciton dissociation, charge transport and collection processes, and thus increase the overall PCE value. Figure 5a shows the UV–vis absorption spectra of the OPV active layer at different concentrations of FeS2 as well as that of the pure FeS2 film. The spectrum of the PTB7

• at 80 °C for at least 12 h. Then, the ITO substrates were treated with UV-ozone plasma for 15 min. A PEDOT:PSS layer of ≈40 nm thickness was spin-coated on top of the ITO substrate at 4500 rpm for 1 min, and then it was thermally treated at 120 °C for 20 min. The active layers with and without FeS2

• acetonitrile using 0.1 M tetrabutylammonium hexafluorophosphate (TBAPF6) as the electrolyte at a scan rate of 100 mVs−1, and each solution was purged with N2 prior to measurement. UV–vis characterization was performed through thin films of the PTB7:PC71BM active layer with and without FeS2 NCs at different

Targeted therapeutic effect against the breast cancer cell line MCF-7 with a CuFe₂O₄/silica/cisplatin nanocomposite formulation

• B. Rabindran Jermy,
• Vijaya Ravinayagam,
• Widyan A. Alamoudi,
• Dana Almohazey,
• Hatim Dafalla,
• Lina Hussain Allehaibi,
• Abdulhadi Baykal,
• Muhammet S. Toprak and
• Thirunavukkarasu Somanathan

Beilstein J. Nanotechnol. 2019, 10, 2217–2228, doi:10.3762/bjnano.10.214

• saline solution. The presence of cubic spinel CuFe2O4 on HYPS was confirmed through powder X-ray diffraction (PXRD), Fourier transform infrared spectroscopy (FTIR) and diffuse reflectance UV–vis spectroscopy (DR UV–vis) analysis. The HYPS particles showed a surface area of 170 m2/g, pore size of 8.3 nm

• dispersive X-ray (EDX) mapping analysis showed the presence of homogeneous silica particles with nanoclusters of copper ferrite distributed on the HYPS support. Vibrating sample magnetometry (VSM) analysis of CuFe2O4/HYPS showed paramagnetic behavior with a saturated magnetization value of 7.65 emu/g. DRS UV

• multifunctional biomedical applications. The crystalline phase, morphology, magnetization, and coordination environment of various spinel species were characterized using X-ray diffraction (XRD), BET surface area measurements, vibrating sample magnetometry (VSM), diffuse reflectance UV–vis spectroscopy (DR UV–vis

Mannosylated brush copolymers based on poly(ethylene glycol) and poly(ε-caprolactone) as multivalent lectin-binding nanomaterials

• Stefania Ordanini,
• Wanda Celentano,
• Anna Bernardi and
• Francesco Cellesi

Beilstein J. Nanotechnol. 2019, 10, 2192–2206, doi:10.3762/bjnano.10.212

• ] (Figure 6A). Glycopolymers were tested in the presence of Con A in HBS buffer at pH 7.4. A fixed mannose concentration 2.5 times higher than the Con A binding site concentration was used, and turbidity was measured using an UV–vis spectrometer (Figure 7). The kinetics of glycopolymer-induced clustering

• use; THF used for click reaction was dried over Na/benzophenone and freshly distilled. Thin-layer chromatography (TLC) was performed on Silica Gel 60 F254 plates (Merck) with UV detection (254 and 365 nm) or using appropriate developing solutions. Flash column chromatography was performed on silica

• A-glycopolymer solution was vigorously stirred for 11 s using a micropipette and then placed in a Jasco V-630 UV–vis spectrometer at 30 °C, using semi-micro disposable cuvettes (optical PS, 2.5 mL volume, 1 cm path length). Optical Density (OD) data were recorded at 420 nm every 12 s for 10 min. t1

Liquid crystal tunable claddings for polymer integrated optical waveguides

• José M. Otón,
• Manuel Caño-García,
• Fernando Gordo,
• Eva Otón,
• Morten A. Geday and
• Xabier Quintana

Beilstein J. Nanotechnol. 2019, 10, 2163–2170, doi:10.3762/bjnano.10.209

• waveguides and their tunability has been demonstrated. Experimental Several organic materials have been evaluated in a previous work [13]. The best results were obtained with direct laser writing (DLW) of UV-curing polymers specifically designed for optical waveguide manufacturing, such as the Ormocore

BergaCare SmartLipids: commercial lipophilic active concentrates for improved performance of dermal products

• Florence Olechowski,
• Rainer H. Müller and
• Sung Min Pyo

Beilstein J. Nanotechnol. 2019, 10, 2152–2162, doi:10.3762/bjnano.10.208

• with Nile red and applied in a square onto the inner forearm. The presence of applied particles was detected using an UV lamp with a wavelength of 365 nm (Figure 6, left). Then the forearms were washed under flowing water and rubbed with the thumb. Most of the nanoemulsion was washed off, whereas the

• cells below and could lead to a higher transepidermal water loss (TEWL). In addition, the skin is more exposed to environmental stress, ranging from UV/IR radiation to pollution from the air, e.g., particulate matter. Especially in the last two years, skin care products/cosmetics with “anti-pollution

• are too high and promote irritation need to be avoided. It was shown for tretinoin, that incorporation into lipid particles avoided skin irritation [33]. Little or no release is ideal for molecular sunscreens for UV protection, which should not penetrate into but remain on the skin, ideally inside the

Improved adsorption and degradation performance by S-doping of (001)-TiO₂

• Xiao-Yu Sun,
• Xian Zhang,
• Xiao Sun,
• Ni-Xian Qian,
• Min Wang and
• Yong-Qing Ma

Beilstein J. Nanotechnol. 2019, 10, 2116–2127, doi:10.3762/bjnano.10.206

• spectra (UV–vis DRS) of the samples were measured on a Shimadazu U-4100 spectrometer (U-4100, Shimadazu Corporation, Tokyo, Japan). X-ray photoelectron spectroscopy (XPS) was performed using a Thermo Scientific ESCALAB 250Xi (Thermo Scientific Inc., USA). The chemical bonds of the photocatalysts were

• a dark room for 30 min to achieve the adsorption–desorption equilibrium. Subsequent to irradiation, samples of the solution were taken every 10 min. After high-speed centrifugation, the concentration of MB was analyzed by a UV–vis spectrometer (UV-3200S, MAPADA, Shanghai, China) and calculated using

• the O 2p orbitals. At the same time, the ratio of the Ov increases in the order of 2-S0.5 < 2-S1 < 2-S5 < 2-S3, as given in Table 3; therefore, the decrease of the DOS mainly results from an increase of the ratio of oxygen vacancies. Figure 6 shows the UV–vis DRS of 2-S0, 2-S0.5, 2-S1, 2-S3 and 2-S5

The importance of design in nanoarchitectonics: multifractality in MACE silicon nanowires

• Stefania Carapezzi and
• Anna Cavallini

Beilstein J. Nanotechnol. 2019, 10, 2094–2102, doi:10.3762/bjnano.10.204

• present work. The procedure to grow the MACE samples is carried out as follows: (100)-oriented Si wafers are the substrates. As a first step, the native oxide is removed from their surfaces by UV-oxidizing (2 min) and then dipping them (5 min) in 5% HF. Subsequently, 2 nm thick Au layers are deposited on

Incorporation of doxorubicin in different polymer nanoparticles and their anticancer activity

• Sebastian Pieper,
• Hannah Onafuye,
• Dennis Mulac,
• Jindrich Cinatl Jr.,
• Mark N. Wass,
• Martin Michaelis and
• Klaus Langer

Beilstein J. Nanotechnol. 2019, 10, 2062–2072, doi:10.3762/bjnano.10.201

• pictures were received at an accelerating voltage of 10,000 V and a working distance of 10 mm (CamScan CS4, Cambridge Scanning Company, Cambridge, UK). Doxorubicin quantification via HPLC-UV The amount of doxorubicin that had been incorporated into the nanoparticles was determined by HPLC-UV (HPLC 1200

Synthesis of highly active ETS-10-based titanosilicate for heterogeneously catalyzed transesterification of triglycerides

• Muhammad A. Zaheer,
• David Poppitz,
• Khavar Feyzullayeva,
• Marianne Wenzel,
• Jörg Matysik,
• Radomir Ljupkovic,
• Aleksandra Zarubica,
• Alexander A. Karavaev,
• Andreas Pöppl,
• Roger Gläser and
• Muslim Dvoyashkin

Beilstein J. Nanotechnol. 2019, 10, 2039–2061, doi:10.3762/bjnano.10.200

• temperatures [52], ion exchange [53][54], UV [55] or γ-irradiation [51]. To characterize the state of Ti in the titanosilicates participating in catalytic tests and the possible presence of impurities, the EPR spectra of these samples were measured at 70 K (Figure 14). The spectrum of the parent K,Na-ETS-10

Optimization and performance of nitrogen-doped carbon dots as a color conversion layer for white-LED applications

• Tugrul Guner,
• Hurriyet Yuce,
• Didem Tascioglu,
• Eren Simsek,
• Umut Savaci,
• Aziz Genc,
• Servet Turan and
• Mustafa M. Demir

Beilstein J. Nanotechnol. 2019, 10, 2004–2013, doi:10.3762/bjnano.10.197

• solid-state lighting, provides a promising strategy to reduce electricity consumption, and WLEDs are expected to replace traditional lighting products in the future [24][25][26][27]. A WLED mainly consists of a blue or UV LED chip and phosphors as color conversion layers [28][29][30][31][32]. A typical

• exfoliation of graphite [47]. The obtained CDots showed a broad band emission due to their heterogeneity in particle size and surface-functional groups. The authors explored the potential of CDots as UV-to-visible color converters using a 365 nm UV chip and could generate white light with CIE color

• source since it is cost-efficient, abundant and nitrogen-rich [54]. Photographic images of the resulting N-CDot suspension illuminated under both natural and UV light are presented in Figure 1b. Fabrication of nitrogen-doped carbon dot films and fibers Production of the composite films The PVP solution

Gold-coated plant virus as computed tomography imaging contrast agent

• Alaa A. A. Aljabali,
• Mazhar S. Al Zoubi,
• Khalid M. Al-Batanyeh,
• Ali Al-Radaideh,
• Mohammad A. Obeid,
• Abeer Al Sharabi,
• Walhan Alshaer,
• Bayan AbuFares,
• Tasnim Al-Zanati,
• Murtaza M. Tambuwala,
• Naveed Akbar and
• David J. Evans

Beilstein J. Nanotechnol. 2019, 10, 1983–1993, doi:10.3762/bjnano.10.195

• particles were dark red in color. Characteristic SPR bands of Au-CPMV were observed in the UV–vis spectrum at λ = 535 nm for particles with a diameter of 50 nm, at λ = 552 nm for particles with a diameter of 70 nm and at λ = 572 nm for particles with a diameter of 100 nm (see below in Figure 3C). This

• 28 nm and a surface charge of ca. 13 mV [38]. Surface functionalization and UV–visible studies One of the objectives of the present work was the development of a smart cell-specific contrast agent based on the surface modification of Au-CPMV with specific antibodies to target desired cells

• purification of the antibody-labeled particles suggesting successful modification of their exterior surface. This observed increase in the hydrodynamic radius is consistent with the previous report of particles coated with proteins [39]. In addition, the UV–vis spectrum was used to evaluate the surface

Porous silver-coated pNIPAM-co-AAc hydrogel nanocapsules

• William W. Bryan,
• Riddhiman Medhi,
• Maria D. Marquez,
• Supparesk Rittikulsittichai,
• Michael Tran and
• T. Randall Lee

Beilstein J. Nanotechnol. 2019, 10, 1973–1982, doi:10.3762/bjnano.10.194

• . The morphology and composition of the composite nanoparticles were characterized by SEM, TEM, and FTIR, respectively. UV–vis spectroscopy was used to characterize the optical properties. Keywords: hydrogels; nanocapsules; photothermal delivery; poly(NIPAM); porous silver shells; Introduction

• modification of the polymer backbone [83][85]. To demonstrate the thermo-responsive behavior of the soft hydrogel polymer core particles, we performed UV–vis spectral analysis on the THPC gold-seeded hydrogel core particles at selected temperatures. Figure 3 shows the UV–vis spectra of the THPC gold-seeded

• (Figure 5b) with overall diameters of ≈920 nm and capsule thicknesses of ≈40 nm. Note also the stepwise size progression of the particles shown in Figure 5c. Optical properties of the porous silver nanocapsules with pNIPAM-co-AAc hydrogel cores. Figure 6 shows the UV–vis extinction spectra of the silver