Recent advances in green carbon dots (2015–2022): synthesis, metal ion sensing, and biological applications

• Aisha Kanwal,
• Naheed Bibi,
• Sajjad Hyder,
• Arif Muhammad,
• Hao Ren,
• Jiangtao Liu and
• Zhongli Lei

Beilstein J. Nanotechnol. 2022, 13, 1068–1107, doi:10.3762/bjnano.13.93

• , and ultrasonic synthesis. In the bottom-up methods, CDs are formed from molecular precursors by various techniques such as hydrothermal treatment [25][26][27][28][29], microwave synthesis [30], and pyrolysis [31]. A tremendous amount of work has been done regarding the synthesis and different

• –31G diffused and polarized basis sets. An excellent agreement was found between theoretical data and experimental results [73]. An ultrasonic-assisted solvent extraction approach was employed to synthesize CDs from rice fried Codonopsis pilosula (CP). The CP-CDs possess good sensitivity and

Interaction between honeybee mandibles and propolis

• Leonie Saccardi,
• Franz Brümmer,
• Jonas Schiebl,
• Oliver Schwarz,
• Alexander Kovalev and
• Stanislav Gorb

Beilstein J. Nanotechnol. 2022, 13, 958–974, doi:10.3762/bjnano.13.84

• was then measured between the two lines. Furthermore, different solvents were used to wash fresh mandibles in order to try removing any potential surface coating. Mandibles were washed in an ultrasonic bath with distilled water for 10 min or with either chloroform (Rotisolv® HPLC stabilised with 1

• to remove hydrophobic substances and the wax layer from mandibles [27]. The ultrasonic bath facilitates the dissolving procedure and particle removal from the surface. To visualise the effect of washing, dry untreated mandibles and mandibles treated with the different solvents were examined using a

Gelatin nanoparticles with tunable mechanical properties: effect of crosslinking time and loading

• Agnes-Valencia Weiss,
• Daniel Schorr,
• Julia K. Metz,
• Metin Yildirim,
• Saeed Ahmad Khan and
• Marc Schneider

Beilstein J. Nanotechnol. 2022, 13, 778–787, doi:10.3762/bjnano.13.68

• experimental triplicate. Atomic force microscopy For AFM measurements, GNPs were electrostatically fixed on positively coated silica specimens. Samples for AFM measurements were prepared according to the following protocol: Silica wafers were cleaned in an ultrasonic bath (Elmasonic B, Elma Schmidbauer GmbH

Reliable fabrication of transparent conducting films by cascade centrifugation and Langmuir–Blodgett deposition of electrochemically exfoliated graphene

• Teodora Vićentić,
• Stevan Andrić,
• Vladimir Rajić and
• Marko Spasenović

Beilstein J. Nanotechnol. 2022, 13, 666–674, doi:10.3762/bjnano.13.58

• wavelength of 660 nm is obtained for these films, which is in agreement with earlier works on Langmuir–Blodgett assembled ultrasonic-assisted liquid-phase exfoliated graphene. Our work demonstrates that films that are in all respects on par with films of graphene obtained through other solution-based

• the range of 1–10 layers, in a range of different liquids, at a wide range of concentrations [13][14]. The mechanism of ultrasonic exfoliation involves ultrasonic waves in liquid media creating bubbles or voids in the liquid, which generate shear forces or cavitation bubbles upon collapsing, which

• size selection is the route to take towards the mass use of 2D materials in solution. Although size selection through post-processing with cascade centrifugation has been demonstrated in the context of ultrasonic LPE materials [30][31], to the best of our knowledge, the method has not been applied to

Antibacterial activity of a berberine nanoformulation

• Hue Thi Nguyen,
• Tuyet Nhung Pham,
• Anh-Tuan Le,
• Nguyen Thanh Thuy,
• Tran Quang Huy and
• Thuy Thi Thu Nguyen

Beilstein J. Nanotechnol. 2022, 13, 641–652, doi:10.3762/bjnano.13.56

• BBR in a 2.0 mL Eppendorf tube containing 1.0 mL of distilled water. The tube was placed in an ultrasonic bath for 30 min at room temperature. Then, the BBR solution was centrifuged at a speed of 5000 rpm for 5 min. The supernatant liquid was withdrawn as saturated BBR solution. Physicochemical

Stimuli-responsive polypeptide nanogels for trypsin inhibition

• Petr Šálek,
• Jana Dvořáková,
• Sviatoslav Hladysh,
• Diana Oleshchuk,
• Ewa Pavlova,
• Jan Kučka and
• Vladimír Proks

Beilstein J. Nanotechnol. 2022, 13, 538–548, doi:10.3762/bjnano.13.45

• solution. The surfactants SPAN 80 (0.855 g) and TWEEN 85 (0.045 g) were dissolved in CHX (20.4 g) and mixed with the aqueous solution of PHEG-Tyr with HRP. This two-phase system was cooled to 0 °C and dispersed using a UP200Ht ultrasonic processor equipped with a sonotrode S26d7 (Hielscher Ultrasonics GmbH

• calculated using the Stokes–Einstein equation. For DLS measurements, both nanogels were dispersed in Q-H2O (2 mL; 1 mg/mL) in glass vials by a UP200Ht ultrasonic processor equipped with a sonotrode Hielscher S26d2 for 5 min at 40% amplitude using the following method: 2 min pulsation (0.5 s pulse rate), 2

Influence of thickness and morphology of MoS₂ on the performance of counter electrodes in dye-sensitized solar cells

• Lam Thuy Thi Mai,
• Hai Viet Le,
• Ngan Kim Thi Nguyen,
• Van La Tran Pham,
• Thu Anh Thi Nguyen,
• Nguyen Thanh Le Huynh and
• Hoang Thai Nguyen

Beilstein J. Nanotechnol. 2022, 13, 528–537, doi:10.3762/bjnano.13.44

• substrates were first cleaned in a 1% Hellmanex solution at 70 °C for 30 min in an ultrasonic bath, then washed three times in distilled water, dried by nitrogen flow, and finally treated in a UV ozone chamber for 5 min to obtain the cleaned FTO electrode. Precursor solutions were prepared by dissolving (NH4

Design and characterization of polymeric microneedles containing extracts of Brazilian green propolis

• Camila Felix Vecchi,
• Rafaela Said dos Santos,
• Jéssica Bassi da Silva and
• Marcos Luciano Bruschi

Beilstein J. Nanotechnol. 2022, 13, 503–516, doi:10.3762/bjnano.13.42

• , which was easy to handle. However, there was intense formation of air bubbles. In order to reduce the bubbles in the final mold, the flask containing the mixture was placed in an ultrasonic bath and, subsequently, in a vacuum desiccator, until all bubbles were removed. With the mixture being completely

Ethosomal (−)-epigallocatechin-3-gallate as a novel approach to enhance antioxidant, anti-collagenase and anti-elastase effects

• Çiğdem Yücel,
• Gökçe Şeker Karatoprak,
• Sena Yalçıntaş and
• Tuğba Eren Böncü

Beilstein J. Nanotechnol. 2022, 13, 491–502, doi:10.3762/bjnano.13.41

• min followed by sonication using an ultrasonic bath (Wise Clean, Korea, 210 W, 40 kHz), at 40% sonication strength, and three cycles of 30 min to obtain monodisperse vesicles and to enhance encapsulation efficiency [44][45]. Then, ETHs were collected by centrifugation at 10.000 rpm for 30 min. For the

Electrostatic pull-in application in flexible devices: A review

• Teng Cai,
• Yuming Fang,
• Yingli Fang,
• Ruozhou Li,
• Ying Yu and
• Mingyang Huang

Beilstein J. Nanotechnol. 2022, 13, 390–403, doi:10.3762/bjnano.13.32

• switch, thus reducing the need for external excitation. Ultrasonic transducers based on capacitive switch structures are widely used in medical imaging, underwater tests, and obstacle detection. Saadatmand and Kook [97] conducted a theoretical analysis on electrostatically driven ultrasonic transducers

• reduce the demand for voltage of electrostatic switches, but would introduce additional manufacturing cost. Rutsch et al. [98] combined piezoelectric materials with NEM switches to prepare ultrasonic transducers, as shown in Figure 12. The structure retained piezoelectric bending and a DC voltage could

• be used to adjust the resonant frequency of the electrostatic switch to expand the bandwidth of the ultrasonic transducer. İkizoğlu et al. [99] combined a piezoelectric energy harvester with a cantilever beam switch for RF systems. Under vibrations, the piezoelectric material produces charges that

Enhancement of the piezoelectric coefficient in PVDF-TrFe/CoFe₂O₄ nanocomposites through DC magnetic poling

• Marco Fortunato,
• Alessio Tamburrano,
• Maria Paola Bracciale,
• Maria Laura Santarelli and
• Maria Sabrina Sarto

Beilstein J. Nanotechnol. 2021, 12, 1262–1270, doi:10.3762/bjnano.12.93

• -Aldrich, ≥99%) with a concentration of 1 wt % and tip-sonicated using an ultrasonic processor in pulsed mode for 20 min at 70% of the power amplitude. Subsequently, the CoFe2O4 suspension was added to a PVDF-TrFE solution (Piezotech FC Ink L, 7 wt %) at the desired ratio. The mixture was bath-sonicated

Use of nanosystems to improve the anticancer effects of curcumin

• Andrea M. Araya-Sibaja,
• Norma J. Salazar-López,
• Krissia Wilhelm Romero,
• José R. Vega-Baudrit,
• J. Abraham Domínguez-Avila,
• Carlos A. Velázquez Contreras,
• Ramón E. Robles-Zepeda,
• Mirtha Navarro-Hoyos and
• Gustavo A. González-Aguilar

Beilstein J. Nanotechnol. 2021, 12, 1047–1062, doi:10.3762/bjnano.12.78

• disadvantages, such as the need for additional instrumentation to generate electromagnetic or ultrasonic waves, which may increase their cost and/or complexity. Curcumin (CUR) or diferuloylmethane is a phenolic compound extracted from turmeric (Curcuma longa) rhizomes. It is safe for human consumption [13] and

Revealing the formation mechanism and band gap tuning of Sb₂S₃ nanoparticles

• Maximilian Joschko,
• Franck Yvan Fotue Wafo,
• Christina Malsi,
• Danilo Kisić,
• Ivana Validžić and
• Christina Graf

Beilstein J. Nanotechnol. 2021, 12, 1021–1033, doi:10.3762/bjnano.12.76

• water. The nanoparticles were redispersed using an ultrasonic bath (Sonorex RK512H (860 W, 35 kHz) from Bandelin). A controlled heating rate and temperature in the reaction vessel was achieved by a temperature controller (LTR 3500, Juchheim Solingen). Injections into the reaction vessel were performed

• precursor, an S-OlAm solution, was produced by dissolving 1.5 mmol elemental sulfur in 6 mL OlAm via sonification in an ultrasonic bath for 10 min. Afterward, 25 mL paraffin oil was added. The solution was heated to 150 °C with a heating rate of 3.3 K/min under magnetic stirring (800 rpm). Second, an Sb(III

A Au/CuNiCoS₄/p-Si photodiode: electrical and morphological characterization

• Adem Koçyiğit,
• Adem Sarılmaz,
• Teoman Öztürk,
• Faruk Ozel and
• Murat Yıldırım

Beilstein J. Nanotechnol. 2021, 12, 984–994, doi:10.3762/bjnano.12.74

• the Al/CuNiCoS4/p-Si device A p-type Si(100) wafer was used as substrate and as semiconductor material for the Au/CuNiCoS4/p-Si photodiode. First, the wafer was cut to 2 cm2 pieces, and acetone and propanol were used to clean the pieces in an ultrasonic cleaner. Then, the pieces were immersed in HF

Modification of a SERS-active Ag surface to promote adsorption of charged analytes: effect of Cu²⁺ ions

• Bahdan V. Ranishenka,
• Andrei Yu. Panarin,
• Irina A. Chelnokova,
• Sergei N. Terekhov,
• Peter Mojzes and
• Vadim V. Shmanai

Beilstein J. Nanotechnol. 2021, 12, 902–912, doi:10.3762/bjnano.12.67

• round bottom flask and stirred until complete dissolution. Then, 640 µL of 4 mg/mL silver nitrate solution were added under vigorous stirring and kept for 4 h in the ultrasonic bath. The resulting silver nanoparticle solution was dialyzed against 2.5 mM sodium citrate and stored at 4 °С. Glass and

Comprehensive review on ultrasound-responsive theranostic nanomaterials: mechanisms, structures and medical applications

• Sepand Tehrani Fateh,
• Lida Moradi,
• Elmira Kohan,
• Michael R. Hamblin and
• Amin Shiralizadeh Dezfuli

Beilstein J. Nanotechnol. 2021, 12, 808–862, doi:10.3762/bjnano.12.64

• ]. Early reports in the field of ultrasonic drug delivery demonstrated that the application of US energy alone could facilitate intracellular delivery of molecules by altering membrane integrity or interfering with the endocytosis process; however, this could also be harmful to the cells under some

• clinical applications, which have been discussed in several papers [23][37][38][39][40][41][42]. US-enhanced drug delivery has several important advantages since it is noninvasive, can be precisely focused and controlled, and can penetrate deep into the body [24]. In addition, ultrasonic waves have some

• between ultrasonic waves and the surrounding tissue result in different mechanical, chemical, and thermal effects, which in turn lead to different biological effects. It is notable that the studies in favor of the endocytosis pathway often used only modest US intensity. In contrast, the studies claiming

9.1% efficient zinc oxide/silicon solar cells on a 50 μm thick Si absorber

• Rafal Pietruszka,
• Bartlomiej S. Witkowski,
• Monika Ozga,
• Katarzyna Gwozdz,
• Ewa Placzek-Popko and
• Marek Godlewski

Beilstein J. Nanotechnol. 2021, 12, 766–774, doi:10.3762/bjnano.12.60

• deionized water. The cleaning process removed impurities from the silicon surface (e.g., fat, powders, and dust). The cleaning process was carried out in an ultrasonic cleaner for 5 min for each of the chemicals. Then, the samples were dried in a stream of nitrogen. Following this stage, aluminium was

Recent progress in actuation technologies of micro/nanorobots

• Ke Xu and
• Bing Liu

Beilstein J. Nanotechnol. 2021, 12, 756–765, doi:10.3762/bjnano.12.59

• frequency higher than the upper limit of human hearing. The ultrasonic bubble gathering effect generated by external ultrasonic fields or the pressure difference generated by the asymmetric structure of a robot body in an ultrasonic field can enable the robot to move. Wang et al. [34] developed metal rod

• -shaped micro/nanorobots in batches by template electrodeposition. Under the action of the ultrasonic field, the robots could achieve velocities up to 200 μm/s. Research has shown that standing ultrasonic waves in the megahertz frequency range can suspend, advance, rotate, arrange, and assemble metal

• microelectrodes in water and solutions of high ionic strength. When the ultrasonic frequency is tuned to generate a vertical standing wave, the metal rod is suspended in the midpoint plane of a cylindrical cell. A rapid axial movement of 200 μm/s of the metal microprobe at the resonance frequency was observed

High-yield synthesis of silver nanowires for transparent conducting PET films

• Gul Naz,
• Hafsa Asghar,
• Muhammad Ramzan,
• Muhammad Arshad,
• Rashid Ahmed,
• Muhammad Bilal Tahir,
• Bakhtiar Ul Haq,
• Nadeem Baig and
• Junaid Jalil

Beilstein J. Nanotechnol. 2021, 12, 624–632, doi:10.3762/bjnano.12.51

• , template reduction (hard and soft templates), and ultrasonic reduction methods [17][18][19][20][21][22]. Lithographic and hard template methods are used to prepare silver nanowires with well-defined dimensions but both methods produce polycrystalline silver nanowires with rough surface, triggering

Impact of GaAs(100) surface preparation on EQE of AZO/Al₂O₃/p-GaAs photovoltaic structures

• Piotr Caban,
• Rafał Pietruszka,
• Jarosław Kaszewski,
• Monika Ożga,
• Bartłomiej S. Witkowski,
• Krzysztof Kopalko,
• Piotr Kuźmiuk,
• Katarzyna Gwóźdź,
• Ewa Płaczek-Popko,
• Krystyna Lawniczak-Jablonska and
• Marek Godlewski

Beilstein J. Nanotechnol. 2021, 12, 578–592, doi:10.3762/bjnano.12.48

• (DIW, 18.2 MΩ·cm at 25 °C). The surface of the samples was prepared in five main stages. The stage 1 (initial cleaning in an ultrasonic cleaner, USC) was performed at approx. 30 °C (acetone/3 min, DIW/1 min, isopropanol/3 min, DIW/1 min), while stages 3 and 4 were conducted at room temperature (RT

Structural and optical characteristics determined by the sputtering deposition conditions of oxide thin films

• Petronela Prepelita,
• Florin Garoi and
• Valentin Craciun

Beilstein J. Nanotechnol. 2021, 12, 354–365, doi:10.3762/bjnano.12.29

• , respectively), in order to precisely control and regulate the flow of gases into the deposition chamber. Quartz (fused silica, NEGS2) slides with dimensions of 2 cm × 2 cm × 0.1 cm were used as substrates. Initially, all substrates were cleaned in an ultrasonic bath to ensure good reproducibility of the

Differences in surface chemistry of iron oxide nanoparticles result in different routes of internalization

• Barbora Svitkova,
• Vlasta Zavisova,
• Veronika Nemethova,
• Martina Koneracka,
• Miroslava Kretova,
• Filip Razga,
• Monika Ursinyova and
• Alena Gabelova

Beilstein J. Nanotechnol. 2021, 12, 270–281, doi:10.3762/bjnano.12.22

• to MNPs in the presence or absence of inhibitors as described above. After the treatment, the number of cells was calculated, cells were harvested and digested using HNO3 (500 μL) in an ultrasonic bath at 85 °C for 2 h. The digests were then diluted with 2% HNO3 in deionized water. The instrumental

Effect of different silica coatings on the toxicity of upconversion nanoparticles on RAW 264.7 macrophage cells

• Cynthia Kembuan,
• Helena Oliveira and
• Christina Graf

Beilstein J. Nanotechnol. 2021, 12, 35–48, doi:10.3762/bjnano.12.3

• reaction vessels were cleaned with hydrofluoric acid (8 vol %) and repeatedly rinsed with water. The nanoparticles were redispersed using an ultrasonic bath operating at 860 W, 35 kHz (Sonorex RK512H, Bandelin). Ultrapure water (filter size = 0.22 μm, R = 18.2 MΩ·cm, Millipore) was used for all synthesis

• 33.3 mL of cyclohexane was used. After sonicating for 10 min, 3.736 mL of Igepal CO-520 was added. After a brief mixing using an ultrasonic bath, 0.331 mL of ammonia water was added, and the dispersion was sonicated again for 20 min. Subsequently, 0.331 mL of TEOS was added and the whole mixture was

PEG/PEI-functionalized single-walled carbon nanotubes as delivery carriers for doxorubicin: synthesis, characterization, and in vitro evaluation

• Shuoye Yang,
• Zhenwei Wang,
• Yahong Ping,
• Yuying Miao,
• Yongmei Xiao,
• Lingbo Qu,
• Lu Zhang,
• Yuansen Hu and
• Jinshui Wang

Beilstein J. Nanotechnol. 2020, 11, 1728–1741, doi:10.3762/bjnano.11.155

• PEG and polyethylenimine (PEI), which contains amino groups, were synthesized (CNTs-PEG-PEI). The length of the SWCNTs was first shortened by ultrasonic scission in different strong acid solutions for improving the dispersion in water. Afterwards, PEG and PEI were grafted onto the CNTs. This

Piezoelectric sensor based on graphene-doped PVDF nanofibers for sign language translation

• Shuai Yang,
• Xiaojing Cui,
• Rui Guo,
• Zhiyi Zhang,
• Shengbo Sang and
• Hulin Zhang

Beilstein J. Nanotechnol. 2020, 11, 1655–1662, doi:10.3762/bjnano.11.148

• concentrated in the bent part of the material, and the potential is generated on the opposite side of the device. Electrospinning is used to manufacture GR-doped PVDF fibers. The overall process is shown in Figure 2a. Firstly, GR is dispersed in dimethylformamide (DMF). After ultrasonic treatment, PVDF powder