Synthesis of nickel/gallium nanoalloys using a dual-source approach in 1-alkyl-3-methylimidazole ionic liquids

• Ilka Simon,
• Julius Hornung,
• Juri Barthel,
• Jörg Thomas,
• Maik Finze,
• Roland A. Fischer and
• Christoph Janiak

Beilstein J. Nanotechnol. 2019, 10, 1754–1767, doi:10.3762/bjnano.10.171

• = 1,5-cyclooctadiene) and GaCp* (Cp* = pentamethylcyclopentadienyl) in the ionic liquid [BMIm][NTf2] selectively yields small intermetallic Ni/Ga nanocrystals of 5 ± 1 nm as derived from transmission electron microscopy (TEM) and high-angle annular dark-field scanning transmission electron microscopy

• annular dark-field scanning transmission electron microscopy (HAADF-STEM) was also performed with the FEI Tecnai G2 F20 electron microscope. All EDX spectra acquired in STEM mode were averaged scans over selected areas of about 100 × 100 nm2. The EDX spectra of an isolated particle were measured at

Fabrication of phase masks from amorphous carbon thin films for electron-beam shaping

• Lukas Grünewald,
• Dagmar Gerthsen and
• Simon Hettler

Beilstein J. Nanotechnol. 2019, 10, 1290–1302, doi:10.3762/bjnano.10.128

• (transmission) electron microscopy (S(T)EM). Phase-modulating thin-film devices (phase masks) made of amorphous silicon nitride are commonly used to generate a wide range of different beam shapes. An additional conductive layer on such a device is required to avoid charging under electron-beam irradiation

• Lukas Grunewald Dagmar Gerthsen Simon Hettler Laboratory for Electron Microscopy, Karlsruhe Institute of Technology (KIT), Engesserstrasse 7, 76131 Karlsruhe, Germany 10.3762/bjnano.10.128 Abstract Background: Electron-beam shaping opens up the possibility for novel imaging techniques in scanning

Alloyed Pt₃M (M = Co, Ni) nanoparticles supported on S- and N-doped carbon nanotubes for the oxygen reduction reaction

• Stéphane Louisia,
• Yohann R. J. Thomas,
• Pierre Lecante,
• Marie Heitzmann,
• M. Rosa Axet,
• Pierre-André Jacques and
• Philippe Serp

Beilstein J. Nanotechnol. 2019, 10, 1251–1269, doi:10.3762/bjnano.10.125

• Co islands (Supporting Information File 1, Figure S7a,b) were identified using the scanning transmission electron microscopy/high-angle annular dark-field imaging (STEM-HAADF) technique. Energy-dispersive X-ray spectroscopy (EDX) analysis on the N-CNT surface or in the Co aggregates confirmed the

Synthesis and characterization of quaternary La(Sr)S–TaS₂ misfit-layered nanotubes

• Marco Serra,
• Erumpukuthickal Ashokkumar Anumol,
• Dalit Stolovas,
• Iddo Pinkas,
• Ernesto Joselevich,
• Reshef Tenne,
• Andrey Enyashin and
• Francis Leonard Deepak

Beilstein J. Nanotechnol. 2019, 10, 1112–1124, doi:10.3762/bjnano.10.111

• electron microscopy (SEM) was done by LEO model Supra 55VP SEM. Transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) were performed on a Titan Themis 80-300 microscope with probe and image spherical aberration (Cs) correctors, at 200 kV. Energy-dispersive X-ray

CuInSe₂ quantum dots grown by molecular beam epitaxy on amorphous SiO₂ surfaces

• Henrique Limborço,
• Pedro M.P. Salomé,
• Rodrigo Ribeiro-Andrade,
• Jennifer P. Teixeira,
• Nicoleta Nicoara,
• Kamal Abderrafi,
• Joaquim P. Leitão,
• Juan C. Gonzalez and
• Sascha Sadewasser

Beilstein J. Nanotechnol. 2019, 10, 1103–1111, doi:10.3762/bjnano.10.110

• , we report CuInSe2 nanodots grown through a vacuum-compatible co-evaporation growth process on an amorphous surface. The density, mean size, and peak optical emission energy of the nanodots can be controlled by changing the growth temperature. Scanning transmission electron microscopy measurements

• almost one order of magnitude. It is clear that with increasing growth temperature coarsening and In re-evaporation might play important roles in the nanodots size distribution. The crystal structure of the nanodots was determined by scanning transmission electron microscopy (STEM) analysis performed on

• this work we present samples prepared at substrate temperatures of 490, 530, and 580 °C; they will be referred to by their growth temperature. Characterization The surface morphology was determined by scanning electron microscopy (SEM) in a FEI Quanta 650 FEG SEM microscope. Scanning transmission

Synthesis of MnO₂–CuO–Fe₂O₃/CNTs catalysts: low-temperature SCR activity and formation mechanism

• Yanbing Zhang,
• Lihua Liu,
• Yingzan Chen,
• Xianglong Cheng,
• Chengjian Song,
• Mingjie Ding and
• Haipeng Zhao

Beilstein J. Nanotechnol. 2019, 10, 848–855, doi:10.3762/bjnano.10.85

• the results of NO conversion and of previous studies [6][16][17]. Scanning transmission electron microscopy STEM and element mapping were adopted to further investigate the morphology of the catalyst. As shown in Figure 5a, bright dots associated to the metal elements can be found, indicating the

Amorphous Ni_xCo_yP-supported TiO₂ nanotube arrays as an efficient hydrogen evolution reaction electrocatalyst in acidic solution

• Yong Li,
• Peng Yang,
• Bin Wang and
• Zhongqing Liu

Beilstein J. Nanotechnol. 2019, 10, 62–70, doi:10.3762/bjnano.10.6

• , transmission electron microscopy, UV–vis diffuse reflection spectroscopy, X-ray photoelectron spectroscopy and scanning transmission electron microscopy/energy-dispersive X-ray spectroscopy were used to characterize the physiochemical properties of the samples. The electrochemical performance was investigated

Accurate control of the covalent functionalization of single-walled carbon nanotubes for the electro-enzymatically controlled oxidation of biomolecules

• Naoual Allali,
• Veronika Urbanova,
• Mathieu Etienne,
• Xavier Devaux,
• Martine Mallet,
• Brigitte Vigolo,
• Jean-Joseph Adjizian,
• Chris P. Ewels,
• Sven Oberg,
• Alexander V. Soldatov,
• Edward McRae,
• Yves Fort,
• Manuel Dossot and
• Victor Mamane

Beilstein J. Nanotechnol. 2018, 9, 2750–2762, doi:10.3762/bjnano.9.257

• −1) and 5 µL of DI (5 mg·mL−1). Afterwards, 5 µL of this mixture were deposited onto the chitosan/HIPCO-Fc modified GCE and allowed to dry at ambient temperature. Analytical techniques: High-resolution transmission electron microscopy (HRTEM) and high-resolution scanning transmission electron

• microscopy (HRSTEM) were performed using a probe aberration-corrected JEOL ARM200 microscope equipped with a cold field emission gun, a JEOL JED2300T energy dispersive X-ray spectrometer (EDS) and a Gatan GIF Quantum energy filter for electron energy loss spectroscopy (EELS). The microscope was operated at

High-temperature magnetism and microstructure of a semiconducting ferromagnetic (GaSb)_1−x(MnSb)_x alloy

• Leonid N. Oveshnikov,
• Elena I. Nekhaeva,
• Alexey V. Kochura,
• Alexander B. Davydov,
• Mikhail A. Shakhov,
• Sergey F. Marenkin,
• Oleg A. Novodvorskii,
• Alexander P. Kuzmenko,
• Alexander L. Vasiliev,
• Boris A. Aronzon and
• Erkki Lahderanta

Beilstein J. Nanotechnol. 2018, 9, 2457–2465, doi:10.3762/bjnano.9.230

• –MnSb alloy films with x = 0.41 and we elucidate the origin of the ferromagnetic state in this material. We use atomic force and magnetic force microscopy (AFM and MFM) as well as scanning/transmission electron microscopy (S/TEM) to study the sample structure. Experimental GaSb–MnSb films with a

Electrospun one-dimensional nanostructures: a new horizon for gas sensing materials

• Muhammad Imran,
• Nunzio Motta and
• Mahnaz Shafiei

Beilstein J. Nanotechnol. 2018, 9, 2128–2170, doi:10.3762/bjnano.9.202

• deposited directly onto a controlled and selective deposition area using a multifield electrospinning setup as shown in Figure 2. The scanning transmission electron microscopy (STEM) image confirms the uniform distribution of MoO3 NPs inside the electrospun fibers. Similarly, CuO NPs are embedded in

Synthesis of rare-earth metal and rare-earth metal-fluoride nanoparticles in ionic liquids and propylene carbonate

• Marvin Siebels,
• Lukas Mai,
• Laura Schmolke,
• Kai Schütte,
• Juri Barthel,
• Junpei Yue,
• Jörg Thomas,
• Bernd M. Smarsly,
• Anjana Devi,
• Roland A. Fischer and
• Christoph Janiak

Beilstein J. Nanotechnol. 2018, 9, 1881–1894, doi:10.3762/bjnano.9.180

• distributions of the nanoparticles were determined by transmission electron microscopy (TEM) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) to an average diameter of (11 ± 6) to (38 ± 17) nm for the REF3-NPs from [BMIm][BF4]. The RE-NPs from [BMIm][NTf2] or PC showed

• nanoparticles were determined by transmission electron microscopy (TEM) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). The crystalline phases and the absence of impurities (oxides) in RE-NPs and REF3-NPs were identified by powder X-ray diffraction (PXRD) and selected

• images were recorded with a Gatan UltraScan 1000P detector. High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) as shown in Figure S4a (Supporting Information File 1) was also performed with this microscope. TEM samples were prepared by drop-casting the diluted material

Optical near-field mapping of plasmonic nanostructures prepared by nanosphere lithography

• Gitanjali Kolhatkar,
• Alexandre Merlen,
• Jiawei Zhang,
• Chahinez Dab,
• Gregory Q. Wallace,
• François Lagugné-Labarthet and
• Andreas Ruediger

Beilstein J. Nanotechnol. 2018, 9, 1536–1543, doi:10.3762/bjnano.9.144

• intensity on the map [31]. The same principle is used with scanning transmission electron microscopy (STEM) and electron energy loss spectroscopy (EELS) [32][33][34]. This technique based on inelastic scattering measures the energy losses of the electrons. At the hot spots, the plasmon excitation results in

Noble metal-modified titania with visible-light activity for the decomposition of microorganisms

• Maya Endo,
• Zhishun Wei,
• Kunlei Wang,
• Baris Karabiyik,
• Kenta Yoshiiri,
• Paulina Rokicka,
• Bunsho Ohtani,
• Agata Markowska-Szczupak and
• Ewa Kowalska

Beilstein J. Nanotechnol. 2018, 9, 829–841, doi:10.3762/bjnano.9.77

• were modified with silver and gold by photodeposition, and characterized by diffuse reflectance spectroscopy (DRS), X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning transmission electron microscopy (STEM). It was found that silver co-existed in zero valent (core) and

Bombyx mori silk/titania/gold hybrid materials for photocatalytic water splitting: combining renewable raw materials with clean fuels

• Stefanie Krüger,
• Michael Schwarze,
• Otto Baumann,
• Christina Günter,
• Michael Bruns,
• Christian Kübel,
• Dorothée Vinga Szabó,
• Rafael Meinusch,
• Verónica de Zea Bermudez and
• Andreas Taubert

Beilstein J. Nanotechnol. 2018, 9, 187–204, doi:10.3762/bjnano.9.21

• TEM with a LaB6 cathode operated at 120 kV. High resolution transmission electron microscopy (HRTEM) was done using an aberration corrected Titan 80-300 (FEI, Eindhoven, The Netherlands) with field emission gun, operated at 300 kV. Scanning transmission electron microscopy (STEM) and chemical analysis

Comparative study of post-growth annealing of Cu(hfac)₂, Co₂(CO)₈ and Me₂Au(acac) metal precursors deposited by FEBID

• Marcos V. Puydinger dos Santos,
• Aleksandra Szkudlarek,
• Artur Rydosz,
• Carlos Guerra-Nuñez,
• Fanny Béron,
• Kleber R. Pirota,
• Stanislav Moshkalev,
• José Alexandre Diniz and
• Ivo Utke

Beilstein J. Nanotechnol. 2018, 9, 91–101, doi:10.3762/bjnano.9.11

• transmission electron microscopy results from as-deposited materials are indicated. On the other hand, the Co grains fully percolate above 200 °C. Top: Raman spectra in the carbon range as a function of the post-growth annealing temperature of (a) Co–C, (b) Cu–C and (c) Au–C deposits, showing the peaks of the

• , while only slight changes are observed in Cu–C and Au–C deposits. SEM-based average diameters of Co, Cu and Au FEBID agglomerates as function of the annealing temperature. At room temperature, Cu and Au agglomerates were visible in SEM but the contrast was too low to quantify the size. Instead, scanning

Material discrimination and mixture ratio estimation in nanocomposites via harmonic atomic force microscopy

• Weijie Zhang,
• Yuhang Chen,
• Xicheng Xia and
• Jiaru Chu

Beilstein J. Nanotechnol. 2017, 8, 2771–2780, doi:10.3762/bjnano.8.276

• characterization of the distribution and mixture ratio of two or more different components at nanoscale resolution is of particular significance because the materials are closely related to the functional performance [3]. Scanning/transmission electron microscopy is commonly applied for the detection of mixed NPs

Direct writing of gold nanostructures with an electron beam: On the way to pure nanostructures by combining optimized deposition with oxygen-plasma treatment

• Domagoj Belić,
• Mostafa M. Shawrav,
• Emmerich Bertagnolli and
• Heinz D. Wanzenboeck

Beilstein J. Nanotechnol. 2017, 8, 2530–2543, doi:10.3762/bjnano.8.253

• ). Once the deposition rate was optimized and the samples were produced, high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM) revealed that the crystallites in the planar deposits were considerably larger than those in NPs (compare Figure 1f to Figure 1c). Although both

Involvement of two uptake mechanisms of gold and iron oxide nanoparticles in a co-exposure scenario using mouse macrophages

• Dimitri Vanhecke,
• Dagmar A. Kuhn,
• Dorleta Jimenez de Aberasturi,
• Sandor Balog,
• Ana Milosevic,
• Dominic Urban,
• Diana Peckys,
• Niels de Jonge,
• Wolfgang J. Parak,
• Alke Petri-Fink and
• Barbara Rothen-Rutishauser

Beilstein J. Nanotechnol. 2017, 8, 2396–2409, doi:10.3762/bjnano.8.239

• a scanning transmission electron microscopy (STEM) detector (described in detail below). The water layer covering the cells was carefully thinned until it was sufficiently thin to allow for the detection of single NPs in a cell with the STEM detector located under the sample. In order to easier

Magnetic properties of optimized cobalt nanospheres grown by focused electron beam induced deposition (FEBID) on cantilever tips

• Soraya Sangiao,
• César Magén,
• Darius Mofakhami,
• Grégoire de Loubens and
• José María De Teresa

Beilstein J. Nanotechnol. 2017, 8, 2106–2115, doi:10.3762/bjnano.8.210

• analyze the chemical composition of the cobalt nanospheres by electron energy loss spectroscopy (EELS) in scanning transmission electron microscopy (STEM) mode and their local magnetic properties by electron holography in a transmission electron microscope (TEM), the specimens were prepared for TEM

AgCl-doped CdSe quantum dots with near-IR photoluminescence

• Pavel A. Kotin,
• Sergey S. Bubenov,
• Natalia E. Mordvinova and
• Sergey G. Dorofeev

Beilstein J. Nanotechnol. 2017, 8, 1156–1166, doi:10.3762/bjnano.8.117

• investigate the location of Ag and Cl in NPs, element distribution maps with the use of energy dispersion X-ray (EDX) spectroscopy were obtained (Figure 5). Figure 5a shows a high angle annular dark field (HAADF) image of sample AgCl_32, which was obtained with the use of scanning transmission electron

• microscopy (STEM). Figure 5–e display the position of Cd, Se, Ag and Cl atoms. The investigation was made on the day of the synthesis of NPs. The colour brightness of one selected pixel is determined by the intensity of L (Cd, Se and Ag) or K (Cl) line in EDX spectrum. The element distribution maps show that

Structural properties and thermal stability of cobalt- and chromium-doped α-MnO₂ nanorods

• Romana Cerc Korošec,
• Polona Umek,
• Alexandre Gloter,
• Jana Padežnik Gomilšek and
• Peter Bukovec

Beilstein J. Nanotechnol. 2017, 8, 1032–1042, doi:10.3762/bjnano.8.104

• the material under X-ray irradiation. The IFEFFIT program package [33] was used for the XANES (X-ray absorption near edge structure) and EXAFS (extended X-ray absorption fine structure) analysis. High-angle annular dark field scanning transmission electron microscopy (HAADF-STEM) images were acquired

• transmission electron microscopy (HAADF-STEM), both shown in Figure 7. The chemical profiles of manganese and oxygen show a correlation with the nanorod shape while the cobalt profile shows more fluctuations due to the rather lower cobalt content (1.3 atom %). Nevertheless, it is clear that cobalt is present

• ). The sulfur detected in the samples is originating from the sulfuric acid that was a part of the reaction mixture [26]. The chemical composition of an individual nanorod (Co-90) was determined using electron energy loss spectroscopy (EELS) in combination with high-angle annular dark field scanning

Ion beam profiling from the interaction with a freestanding 2D layer

• Ivan Shorubalko,
• Kyoungjun Choi,
• Michael Stiefel and
• Hyung Gyu Park

Beilstein J. Nanotechnol. 2017, 8, 682–687, doi:10.3762/bjnano.8.73

• beam source. For imaging the milled pores we use scanning electron microscopy (SEM), scanning transmission electron microscopy (STEM) and helium ion microscopy (HIM). All methods give similar results regarding the measured focused ion beam profiles. Finally, we discuss technical limitations and

Self-assembly of silicon nanowires studied by advanced transmission electron microscopy

• Marta Agati,
• Guillaume Amiard,
• Vincent Le Borgne,
• Paola Castrucci,
• Richard Dolbec,
• Maurizio De Crescenzi,
• My Alì El Khakani and
• Simona Boninelli

Beilstein J. Nanotechnol. 2017, 8, 440–445, doi:10.3762/bjnano.8.47

• Dipartimento di Fisica, Università di Roma “Tor Vergata”, Via della Ricerca Scientifica 1, Roma 00133, Italy, Tekna Plasma Systems Inc., 2935 Industrial Blvd., Sherbrooke QC-J1L 2T9, Canada 10.3762/bjnano.8.47 Abstract Scanning transmission electron microscopy (STEM) was successfully applied to the analysis

Role of oxygen in wetting of copper nanoparticles on silicon surfaces at elevated temperature

• Tapas Ghosh and
• Biswarup Satpati

Beilstein J. Nanotechnol. 2017, 8, 425–433, doi:10.3762/bjnano.8.45

• the high-angle annular dark-field scanning transmission electron microscopy (STEM-HAADF). After the TEM analysis, the same samples were transferred to a rapid thermal annealing unit (model: JETFIRST100 jipelec) and annealing was performed in air, oxygen and nitrogen atmospheres, one by one. The rapid

Influence of hydrofluoric acid treatment on electroless deposition of Au clusters

• Rachela G. Milazzo,
• Antonio M. Mio,
• Giuseppe D’Arrigo,
• Emanuele Smecca,
• Alessandra Alberti,
• Gabriele Fisichella,
• Filippo Giannazzo,
• Corrado Spinella and
• Emanuele Rimini

Beilstein J. Nanotechnol. 2017, 8, 183–189, doi:10.3762/bjnano.8.19

• plating solution. The morphology of gold was examined with plan view TEM and scanning transmission electron microscopy (STEM) in high-angle annular dark-field imaging (HAADF) Z-contrast (atomic number) imaging mode, while the crystalline structure was analyzed in detail with X-ray diffraction. Figure 4a