Structural and optical characteristics determined by the sputtering deposition conditions of oxide thin films

• Petronela Prepelita,
• Florin Garoi and
• Valentin Craciun

Beilstein J. Nanotechnol. 2021, 12, 354–365, doi:10.3762/bjnano.12.29

• diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), while the surface topography of the samples was analyzed using scanning electron microscopy (SEM). The optical characteristics were measured for samples with the same composition but obtained with different deposition parameters, such as increasing

Exploring the fabrication and transfer mechanism of metallic nanostructures on carbon nanomembranes via focused electron beam induced processing

• Christian Preischl,
• Linh Hoang Le,
• Elif Bilgilisoy,
• Armin Gölzhäuser and
• Hubertus Marbach

Beilstein J. Nanotechnol. 2021, 12, 319–329, doi:10.3762/bjnano.12.26

• performed in a commercial UHV system (Multiscanlab, Omicron Nanotechnology, Germany) with a base pressure of p < 2 × 10−10 mbar. The main component of the system is a UHV-compatible electron column (Leo Gemini) for scanning electron microscopy (SEM, nominal resolution better than 3 nm) and a local AES using

The nanomorphology of cell surfaces of adhered osteoblasts

• Christian Voelkner,
• Mirco Wendt,
• Regina Lange,
• Max Ulbrich,
• Martina Gruening,
• Susanne Staehlke,
• Barbara Nebe,
• Ingo Barke and
• Sylvia Speller

Beilstein J. Nanotechnol. 2021, 12, 242–256, doi:10.3762/bjnano.12.20

• cellular rims, while this type of extensions was frequently observed on rough or microstructured surfaces. Ruffles observed by SEM Osteoblastic cells have been studied extensively by scanning electron microscopy (SEM) [32][33][46]. Electron microscopy can yield nanoscopic resolution but requires invasive

• room temperature. Measurement principle and data preparation Scanning electron microscopy (SEM) was performed using a field-emission SEM (Gemini Supra 25, Zeiss) at 1 keV electron energy without Au coating. For SICM a commercial AFM/SICM setup (NX-bio, Park Systems, Korea) with a live-cell chamber (5

Imaging of SARS-CoV-2 infected Vero E6 cells by helium ion microscopy

• Natalie Frese,
• Patrick Schmerer,
• Martin Wortmann,
• Matthias Schürmann,
• Matthias König,
• Michael Westphal,
• Friedemann Weber,
• Holger Sudhoff and
• Armin Gölzhäuser

Beilstein J. Nanotechnol. 2021, 12, 172–179, doi:10.3762/bjnano.12.13

• , while many more cell lines have been reported to be refractory to SARS-CoV-2 infection [15]. Both scanning electron microscopy (SEM) and transmission electron microscopy (TEM) have been used to image SARS-CoV-2 [16][17][18][19][20]. While TEM achieves unsurpassed resolution and can visualize

Mapping the local dielectric constant of a biological nanostructured system

• Wescley Walison Valeriano,
• Rodrigo Ribeiro Andrade,
• Juan Pablo Vasco,
• Angelo Malachias,
• Bernardo Ruegger Almeida Neves,
• Paulo Sergio Soares Guimarães and
• Wagner Nunes Rodrigues

Beilstein J. Nanotechnol. 2021, 12, 139–150, doi:10.3762/bjnano.12.11

• . The scanning electron microscopy (SEM) image presented in Figure 2 shows the nanostructured section of a fragment of the red region indicated in Figure 1a. The section was partially polished using a focused ion beam (FIB) and the multilayered structure is clearly visible. The corrugated surface is the

A review on the green and sustainable synthesis of silver nanoparticles and one-dimensional silver nanostructures

• Sina Kaabipour and
• Shohreh Hemmati

Beilstein J. Nanotechnol. 2021, 12, 102–136, doi:10.3762/bjnano.12.9

Fusion of purple membranes triggered by immobilization on carbon nanomembranes

• René Riedel,
• Natalie Frese,
• Fang Yang,
• Martin Wortmann,
• Raphael Dalpke,
• Daniel Rhinow,
• Norbert Hampp and
• Armin Gölzhäuser

Beilstein J. Nanotechnol. 2021, 12, 93–101, doi:10.3762/bjnano.12.8

• histidine-tag at the extracellular side of a PM mutant (c-His PM). The functionalization and the resulting hybrid membrane were examined by atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), confocal laser scanning microscopy (CLSM), and infrared

Towards 3D self-assembled rolled multiwall carbon nanotube structures by spontaneous peel off

• Jonathan Quinson

Beilstein J. Nanotechnol. 2020, 11, 1865–1872, doi:10.3762/bjnano.11.168

• substrates remain dark, which indicates that MWCNTs are still present. In order to characterize the nature of the peeled-off layer, scanning electron microscopy (SEM) characterization was performed. Figure 1 displays an SEM micrograph of a sample with a C1/N2/C3/N4 structure in which the peeling off was

Self-standing heterostructured NiC_x-NiFe-NC/biochar as a highly efficient cathode for lithium–oxygen batteries

• Shengyu Jing,
• Xu Gong,
• Shan Ji,
• Linhui Jia,
• Bruno G. Pollet,
• Sheng Yan and
• Huagen Liang

Beilstein J. Nanotechnol. 2020, 11, 1809–1821, doi:10.3762/bjnano.11.163

• PANalytical B.V. Empyean X-ray diffractometer with Cu Kα radiation (λ = 1.5406 Å). The surface morphology of the film catalyst was studied via scanning electron microscopy (SEM) on a Carl Zeiss Ultra Plus scanning electron microscope. Transmission electron microscopy (TEM), high-resolution TEM (HR-TEM), and

Electron beam-induced deposition of platinum from Pt(CO)₂Cl₂ and Pt(CO)₂Br₂

• Aya Mahgoub,
• Hang Lu,
• Rachel M. Thorman,
• Konstantin Preradovic,
• Titel Jurca,
• Lisa McElwee-White,
• Howard Fairbrother and
• Cornelis W. Hagen

Beilstein J. Nanotechnol. 2020, 11, 1789–1800, doi:10.3762/bjnano.11.161

• -dispersive X-ray spectroscopy (EDX); focused electron beam-induced deposition (FEBID); nanofabrication; platinum precursors; scanning electron microscopy (SEM); thermogravimetric analysis (TGA); Introduction Focused electron beam-induced deposition (FEBID) is a direct-write nanopatterning technique. FEBID

A self-powered, flexible ultra-thin Si/ZnO nanowire photodetector as full-spectrum optical sensor and pyroelectric nanogenerator

• Liang Chen,
• Jianqi Dong,
• Miao He and
• Xingfu Wang

Beilstein J. Nanotechnol. 2020, 11, 1623–1630, doi:10.3762/bjnano.11.145

• PD based on a p-Si/n-ZnO NWs heterojunction is illustrated in Figure 1a. A typical cross-sectional scanning electron microscopy (SEM) image of the as-grown Si/ZnO NWs heterojunction is shown in Figure 1b. The uniformly grown ZnO NWs are conducive to a stable short-circuit current output. The detailed

Oxidation of Au/Ag films by oxygen plasma: phase separation and generation of nanoporosity

• Abdel-Aziz El Mel,
• Said A. Mansour,
• Mujaheed Pasha,
• Atef Zekri,
• Janarthanan Ponraj,
• Akshath Shetty and
• Yousef Haik

Beilstein J. Nanotechnol. 2020, 11, 1608–1614, doi:10.3762/bjnano.11.143

• formation of unique features, consisting of silver oxide nanoporous microspheres (Figure 1). Our observation was supported by various characterization techniques, including scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction spectroscopy (XRD). We conducted our

High-responsivity hybrid α-Ag₂S/Si photodetector prepared by pulsed laser ablation in liquid

• Raid A. Ismail,
• Hanan A. Rawdhan and
• Duha S. Ahmed

Beilstein J. Nanotechnol. 2020, 11, 1596–1607, doi:10.3762/bjnano.11.142

• ) mixed with cationic cetyltrimethylammonium bromide (CTAB) as surfactant. The effect of the CTAB surfactant on the structural, morphological, optical, and elemental composition of Ag2S NPs was evaluated using X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy

• (SEM), energy-dispersive X-ray spectroscopy (EDX), and UV–vis spectroscopy. The optical absorption decreased and the optical energy gap of α-Ag2S increased from 1.5 to 2 eV after the CTAB surfactant was added to the Tu solution. XRD studies revealed that the synthesized Ag2S NPs were polycrystalline

Fabrication of nano/microstructures for SERS substrates using an electrochemical method

• Jingran Zhang,
• Tianqi Jia,
• Xiaoping Li,
• Junjie Yang,
• Zhengkai Li,
• Guangfeng Shi,
• Xinming Zhang and
• Zuobin Wang

Beilstein J. Nanotechnol. 2020, 11, 1568–1576, doi:10.3762/bjnano.11.139

• three-dimensional topographies of the nanopores. Imaging was performed in contact mode and an elastic constant of 0.2 N/m was selected for the silicon cantilever. The scanning area was 50 × 50 μm2. In addition, a scanning electron microscopy (SEM) system (Zeiss, Germany) was employed to characterize the

Electrokinetic characterization of synthetic protein nanoparticles

• Daniel F. Quevedo,
• Cody J. Lentz,
• Adriana Coll de Peña,
• Yazmin Hernandez,
• Nahal Habibi,
• Rikako Miki,
• Joerg Lahann and
• Blanca H. Lapizco-Encinas

Beilstein J. Nanotechnol. 2020, 11, 1556–1567, doi:10.3762/bjnano.11.138

• electrohydrodynamic jetting process, which was used to prepare SPNPs with a single compartment (identical jetting solutions are flown through the needle) as well as two compartments (parallel flow of two different jetting solutions). (b) A scanning electron microscopy (SEM) image demonstrating the morphology of the

Analysis of catalyst surface wetting: the early stage of epitaxial germanium nanowire growth

• Owen C. Ernst,
• Felix Lange,
• David Uebel,
• Thomas Teubner and
• Torsten Boeck

Beilstein J. Nanotechnol. 2020, 11, 1371–1380, doi:10.3762/bjnano.11.121

• the results for gold droplet formation on Si(111). A decrease in droplet number and an increase in droplet diameter with increasing temperature can be visualized. The droplet diameter distribution is described by a LSW distribution. Figure 3 shows scanning electron microscopy (SEM) and transmission

Structure and electrochemical performance of electrospun-ordered porous carbon/graphene composite nanofibers

• Yi Wang,
• Yanhua Song,
• Chengwei Ye and
• Lan Xu

Beilstein J. Nanotechnol. 2020, 11, 1280–1290, doi:10.3762/bjnano.11.112

• electron microscopy (SEM) under a field-emission scanning electron microscope (FE-SEM) (Hitachi, S4800, Japan). The structural characteristics of the CNFs were observed via transmission electron microscopy (TEM) (FEI, Tecnai G20, Japan). The diameter values of the CNFs were measured using ImageJ software

• . Afterwards, the tube furnace was cooled to room temperature to obtain CCGNFs, which could be directly used as electrodes. For comparison, disordered CGCNFs were also prepared using electrospinning and carbonization techniques. Material characterization The morphology of the CNFs was investigated via scanning

Gas sorption porosimetry for the evaluation of hard carbons as anodes for Li- and Na-ion batteries

• Yuko Matsukawa,
• Fabian Linsenmann,
• Maximilian A. Plass,
• George Hasegawa,
• Katsuro Hayashi and
• Tim-Patrick Fellinger

Beilstein J. Nanotechnol. 2020, 11, 1217–1229, doi:10.3762/bjnano.11.106

• . The morphologies of the HT samples are very similar (Figure 1), but show a different morphology compared to the RF carbons (Supporting Information File 1, Figure S6). Scanning electron microscopy (SEM) imaging reveals spherical particles, morphologically similar to previously reported HCs derived from

• Ventus 532 nm laser using a power of 25 mW at an exposure time of 10 s), respectively. To investigate the morphology of the samples, scanning electron microscopy (SEM) measurements were performed on a scanning electron microscope (NEOSCOPE JCM-6000, JEOL, Japan, equipped with a tungsten filament at 15 kV

Gram-scale synthesis of splat-shaped Ag–TiO₂ nanocomposites for enhanced antimicrobial properties

• Mohammad Jaber,
• Asim Mushtaq,
• Kebiao Zhang,
• Jindan Wu,
• Dandan Luo,
• Zihan Yi,
• M. Zubair Iqbal and
• Xiangdong Kong

Beilstein J. Nanotechnol. 2020, 11, 1119–1125, doi:10.3762/bjnano.11.96

• Rigaku D/Max 2500 powder diffractometer with Cu Kα radiation (λ = 1.5406 Å). Scanning electron microscopy (SEM, JSM5610LV, JEOL, Japan) was used to observed the morphology of the Ag–TiO2 NPs. The sample components were examined by energy-dispersive X-ray spectroscopy. Fourier-transform infrared

Plant growth regulation by seed coating with films of alginate and auxin-intercalated layered double hydroxides

• Vander A. de Castro,
• Valber G. O. Duarte,
• Danúbia A. C. Nobre,
• Geraldo H. Silva,
• Vera R. L. Constantino,
• Frederico G. Pinto,
• Willian R. Macedo and
• Jairo Tronto

Beilstein J. Nanotechnol. 2020, 11, 1082–1091, doi:10.3762/bjnano.11.93

• with indefinitely coherent fragments [28][29]. The volume and average pore diameter values are characteristic of a mesoporous material. Scanning electron microscopy (SEM) images of NAA and ZnAl-NAA-LDH, presented in Figure 4, show the presence of particles with a smooth surface, probably resulting from

Microwave-induced electric discharges on metal particles for the synthesis of inorganic nanomaterials under solvent-free conditions

• Vijay Tripathi,
• Harit Kumar,
• Anubhav Agarwal and
• Leela S. Panchakarla

Beilstein J. Nanotechnol. 2020, 11, 1019–1025, doi:10.3762/bjnano.11.86

• of Cu2O after acid treatment, while the majority of Cu remains in the metallic form (Figure 1a). Scanning electron microscopy (SEM) images of copper powder before and after acid treatment are shown in Figure 1b and Figure 1c, respectively. The SEM image clearly shows the sharp edges on acid-treated

A 3D-polyphenylalanine network inside porous alumina: Synthesis and characterization of an inorganic–organic composite membrane

• Jonathan Stott and
• Jörg J. Schneider

Beilstein J. Nanotechnol. 2020, 11, 938–951, doi:10.3762/bjnano.11.78

• hydrolyzed monomers or an alternative polymerization mechanism [40][41]. The characterization of these composite materials was performed by NIR-spectroscopy (NIR), water contact angle measurements (CA), scanning electron microscopy (SEM) and thermogravimetric (TG) measurements. Mid- and near-infrared

• electron microscopy (SEM), near-infrared spectroscopy (NIR) and contact angle measurements (CA) reveals a change in morphology of the grafted polymer films, which is due to the rearrangement of the secondary structure of the polypeptides. No significant loss of the surface-grafted polypeptides was

• -dimensional fibrillar network with intrinsic porosity was formed in DCM, whereas in THF, a dense and smooth polypeptide film was observed. A post-treatment with a mixture of chloroform and dichloroacetic acid leads to rearrangement of the morphology of the grafted polymer films. The analysis by scanning

Nickel nanoparticles supported on a covalent triazine framework as electrocatalyst for oxygen evolution reaction and oxygen reduction reactions

• Secil Öztürk,
• Yu-Xuan Xiao,
• Dennis Dietrich,
• Beatriz Giesen,
• Juri Barthel,
• Jie Ying,
• Xiao-Yu Yang and
• Christoph Janiak

Beilstein J. Nanotechnol. 2020, 11, 770–781, doi:10.3762/bjnano.11.62

• for CTF-1-600 (see Table S2, Supporting Information File 1, for details). Elemental analyses, thermogravimetric analyses (TGA) and scanning electron microscopy (SEM) characterization data of the materials can be found in Table S1 and Figures S3–S5 in Supporting Information File 1. Synthesis and

• suppressed conductivity detection. Karl-Fischer titration (KFT) was carried out with an ECH/ANALYTIK JENA AQUA 40:00 Karl Fischer titrator. A Carbolite Gero tube furnace has been used for the CTF synthesis. Scanning electron microscopy (SEM) images were recorded with a Jeol JSM-65 10 LV QSEM advanced

A novel dry-blending method to reduce the coefficient of thermal expansion of polymer templates for OTFT electrodes

• Xiangdong Ye,
• Bo Tian,
• Yuxuan Guo,
• Fan Fan and
• Anjiang Cai

Beilstein J. Nanotechnol. 2020, 11, 671–677, doi:10.3762/bjnano.11.53

• the silicon template. Characterization The surface morphology of the PDMS/SiO2 composite template and the OTFT electrodes was investigated via scanning electron microscopy (SEM, JSM-6390a, Japan). The thermal expansion of the PDMS/SiO2 composite template was examined using a thermomechanical analyzer

Preparation, characterization and photocatalytic performance of heterostructured CuO–ZnO-loaded composite nanofiber membranes

• Wei Fang,
• Liang Yu and
• Lan Xu

Beilstein J. Nanotechnol. 2020, 11, 631–650, doi:10.3762/bjnano.11.50

• investigated using scanning electron microscopy (SEM, Hitachi S-4800, Japan). The matrix morphology and fiber diameter distribution were determined using the Image J software (National Institute of Mental Health, Bethesda, Maryland, USA). The diameter of 100 randomly selected fibers in each sample were chosen